Heterostructured g-CN/TiO2 Photocatalysts Prepared by Thermolysis of g-CN/MIL-125(Ti) Composites for Efficient Pollutant Degradation and Hydrogen Production.

Photocatalysts composed of graphitic carbon nitride (g-CN) and TiO2 were efficiently prepared by thermolysis of the MIL-125(Ti) metal organic framework deposited on g-CN. The heterojunction between the 12 nm-sized TiO2 nanoparticles and g-CN was well established and the highest photocatalytic activity was observed for the g-CN/TiO2 (3:1) material. The g-CN/TiO2 (3:1) composite exhibits high visible light performances both for the degradation of pollutants like the Orange II dye or tetracycline but also for the production of hydrogen (hydrogen evolution rate (HER) up to 1330 µmolh-1g-1 and apparent quantum yield of 0.22% using NiS as a cocatalyst). The improved visible light performances originate from the high specific surface area of the photocatalyst (86 m2g-1) and from the efficient charge carriers separation as demonstrated by photoluminescence, photocurrent measurements, and electrochemical impedance spectroscopy. The synthetic process developed in this work is based on the thermal decomposition of metal organic framework deposited on a graphitic material and holds huge promise for the preparation of porous heterostructured photocatalysts.

CdSe nanorod/TiO2 nanoparticle heterojunctions with enhanced solar- and visible-light photocatalytic activity.

CdSe nanorods (NRs) with an average length of ≈120 nm were prepared by a solvothermal process and associated to TiO2 nanoparticles (Aeroxide® P25) by annealing at 300 °C for 1 h. The content of CdSe NRs in CdSe/TiO2 composites was varied from 0.5 to 5 wt %. The CdSe/TiO2 heterostructured materials were characterized by XRD, TEM, SEM, XPS, UV-visible spectroscopy and Raman spectroscopy. TEM images and XRD patterns show that CdSe NRs with wurtzite structure are associated to TiO2 particles. The UV-visible spectra demonstrate that the narrow bandgap of CdSe NRs serves to increase the photoresponse of CdSe/TiO2 composites until ≈725 nm. The CdSe (2 wt %)/TiO2 composite exhibits the highest photocatalytic activity for the degradation of rhodamine B in aqueous solution under simulated sunlight or visible light irradiation. The enhancement in photocatalytic activity likely originates from CdSe sensitization of TiO2 and the heterojunction between these materials which facilitates electron transfer from CdSe to TiO2. Due to its high stability (up to ten reuses without any significant loss in activity), the CdSe/TiO2 heterostructured catalysts show high potential for real water decontamination.

High performance Ce-doped ZnO nanorods for sunlight-driven photocatalysis.

Ce-doped ZnO (ZnO:Ce) nanorods have been prepared through a solvothermal method and the effects of Ce-doping on the structural, optical and electronic properties of ZnO rods were studied. ZnO:Ce rods were characterized by XRD, SEM, TEM, XPS, BET, DRS and Raman spectroscopy. 5% Ce-doped ZnO rods with an average length of 130 nm and a diameter of 23 nm exhibit the highest photocatalytic activity for the degradation of the Orange II dye under solar light irradiation. The high photocatalytic activity is ascribed to the substantially enhanced light absorption in the visible region, to the high surface area of ZnO:Ce rods and to the effective electron-hole pair separation originating from Ce doping. The influence of various experimental parameters like the pH, the presence of salts and of organic compounds was investigated and no marked detrimental effect on the photocatalytic activity was observed. Finally, recyclability experiments demonstrate that ZnO:Ce rods are a stable solar-light photocatalyst.