Coherent Spin Dynamics of Electrons in CdSe Colloidal Nanoplatelets.

Coherent spin dynamics of electrons in CdSe colloidal nanoplatelets are investigated by time-resolved pump-probe Faraday rotation at room and cryogenic temperatures. We measure electron spin precession in a magnetic field and determine g-factors of 1.83 and 1.72 at low temperatures for nanoplatelets with a thickness of 3 and 4 monolayers, respectively. The dephasing time of spin precession T2* amounts to a few nanoseconds and has a weak dependence on temperature, while the longitudinal spin relaxation time T1 exceeds 10 ns even at room temperature. Observations of single and double electron spin-flips confirm that the nanoplatelets are negatively charged. The spin-flip Raman scattering technique reveals g-factor anisotropy by up to 10% in nanoplatelets with thicknesses of 3, 4, and 5 monolayers. In the ensemble with a random orientation of nanoplatelets, our theoretical analysis shows that the measured Larmor precession frequency corresponds to the in-plane electron g-factor. We conclude that the experimentally observed electron spin dephasing and its acceleration in the magnetic field are not provided by the electron g-factor anisotropy and can be related to the localization of the resident electrons and fluctuations of the localization potential.

A Comparative Study of the Band-Edge Exciton Fine Structure in Zinc Blende and Wurtzite CdSe Nanocrystals.

In this paper, we studied the role of the crystal structure in spheroidal CdSe nanocrystals on the band-edge exciton fine structure. Ensembles of zinc blende and wurtzite CdSe nanocrystals are investigated experimentally by two optical techniques: fluorescence line narrowing (FLN) and time-resolved photoluminescence. We argue that the zero-phonon line evaluated by the FLN technique gives the ensemble-averaged energy splitting between the lowest bright and dark exciton states, while the activation energy from the temperature-dependent photoluminescence decay is smaller and corresponds to the energy of an acoustic phonon. The energy splittings between the bright and dark exciton states determined using the FLN technique are found to be the same for zinc blende and wurtzite CdSe nanocrystals. Within the effective mass approximation, we develop a theoretical model considering the following factors: (i) influence of the nanocrystal shape on the bright-dark exciton splitting and the oscillator strength of the bright exciton, and (ii) shape dispersion in the ensemble of the nanocrystals. We show that these two factors result in similar calculated zero-phonon lines in zinc blende and wurtzite CdSe nanocrystals. The account of the nanocrystals shape dispersion allows us to evaluate the linewidth of the zero-phonon line.

Electron Spin Coherence in CdSe Nanocrystals in a Glass Matrix.

The coherent spin dynamics of electrons in CdSe nanocrystals embedded in a glass matrix with diameters from 3.3 up to 6.1 nm are investigated by time-resolved Faraday ellipticity at room and cryogenic temperatures. Only one Larmor precession frequency is detected, which corresponds to the larger of the two precession frequencies and thus g-factor values found in the typical signal from solution-grown colloidal CdSe nanocrystals. We identify this frequency accordingly as associated with the spin precession of resident electrons localized in the nanocrystals in the vicinity of the surface. We provide a detailed theoretical analysis of the exciton level spin structure in the magnetic field and model the spin dynamics in CdSe nanocrystals of different symmetries. This allows us to exclude the exciton as the origin of the experimentally observed oscillating signal. At a cryogenic temperature of 6 K, an additional nonoscillating component emerges in the spin dynamics. We consider several possible origins of this signal and conclude that it is related to the hole spin polarization.

General Expression for the Size-Dependent Optical Properties of Quantum Dots.

While initial theories on quantum confinement in colloidal quantum dots (QDs) led to analytical band gap/size relations or sizing functions, numerical methods describe size quantization more accurately. However, because of the lack of reliable sizing functions, researchers fit experimental band gap/size data sets using models with redundant, physically meaningless parameters that break down upon extrapolation. Here, we propose a new sizing function based on a proportional correction for nonparabolic bands. Using known bulk parameters, we predict size quantization for groups IV, III-V, II-VI, and IV-VI and metal-halide perovskite semiconductors, including straightforward adaptations for negative-gap semiconductors and nonspherical QDs. Refinement with respect to experimental data is possible using the Bohr diameter as a fitting parameter, by which we show a statistically relevant difference in the band gap/size relation for wurtzite and zinc blende CdSe. The general sizing function proposed here unifies the QD size calibration and enables researchers to assess bulk semiconductor parameters and predict the size quantization in unexplored materials.

Polarized emission of CdSe nanocrystals in magnetic field: the role of phonon-assisted recombination of the dark exciton.

The recombination dynamics and spin polarization of excitons in CdSe nanocrystals synthesized in a glass matrix are investigated using polarized photoluminescence in high magnetic fields up to 30 Tesla. The dynamics are accelerated by increasing temperature and magnetic field, confirming the dark exciton nature of low-temperature photoluminescence (PL). The circularly polarized PL in magnetic fields reveals several unusual appearances: (i) a spectral dependence of the polarization degree, (ii) its low saturation value, and (iii) a stronger intensity of the Zeeman component which is higher in energy. The latter feature is the most surprising being in contradiction with the thermal population of the exciton spin sublevels. The same contradiction was previously observed in the ensemble of wet-chemically synthesized CdSe nanocrystals but was not understood. We present a theory which explains all the observed features and shows that the inverted ordering of the circularly polarized PL maxima from the ensemble of nanocrystals is a result of competition between the zero phonon (ZPL) and one optical phonon-assisted (1PL) emission of the dark excitons. The essential aspects of the theoretical model are different polarization properties of the dark exciton emission via ZPL and 1PL recombination channels and the inhomogeneous broadening of the PL spectrum from the ensemble of nanocrystals exceeding the optical phonon energy.

Magneto-Optics of Excitons Interacting with Magnetic Ions in CdSe/CdMnS Colloidal Nanoplatelets.

Excitons in diluted magnetic semiconductors represent excellent probes for studying the magnetic properties of these materials. Various magneto-optical effects, which depend sensitively on the exchange interaction of the excitons with the localized spins of the magnetic ions can be used for probing. Here, we study core/shell CdSe/(Cd,Mn)S colloidal nanoplatelets hosting diluted magnetic semiconductor layers. The inclusion of the magnetic Mn2+ ions is evidenced by three magneto-optical techniques using high magnetic fields up to 15 T: polarized photoluminescence, optically detected magnetic resonance, and spin-flip Raman scattering. We show that the holes in the excitons play the dominant role in exchange interaction with magnetic ions. We suggest and test an approach for evaluation of the Mn2+ concentration based on the spin-lattice relaxation dynamics of the Mn2+ spin system.

Surface spin magnetism controls the polarized exciton emission from CdSe nanoplatelets.

The surface of nominally diamagnetic colloidal CdSe nanoplatelets can demonstrate paramagnetic behaviour owing to the uncompensated spins of dangling bonds, as we reveal here by optical spectroscopy in high magnetic fields up to 15 T using the exciton spin as a probe of the surface magnetism. The strongly nonlinear magnetic field dependence of the circular polarization of the exciton emission is determined by the magnetization of the dangling-bond spins (DBSs), the exciton spin polarization as well as the spin-dependent recombination of dark excitons. The sign of the exciton-DBS exchange interaction depends on the nanoplatelet growth conditions.

Electron and Hole g-Factors and Spin Dynamics of Negatively Charged Excitons in CdSe/CdS Colloidal Nanoplatelets with Thick Shells.

We address spin properties and spin dynamics of carriers and charged excitons in CdSe/CdS colloidal nanoplatelets with thick shells. Magneto-optical studies are performed by time-resolved and polarization-resolved photoluminescence, spin-flip Raman scattering and picosecond pump-probe Faraday rotation in magnetic fields up to 30 T. We show that at low temperatures the nanoplatelets are negatively charged so that their photoluminescence is dominated by radiative recombination of negatively charged excitons (trions). Electron g-factor of 1.68 is measured, and heavy-hole g-factor varying with increasing magnetic field from -0.4 to -0.7 is evaluated. Hole g-factors for two-dimensional structures are calculated for various hole confining potentials for cubic- and wurtzite lattice in CdSe core. These calculations are extended for various quantum dots and nanoplatelets based on II-VI semiconductors. We developed a magneto-optical technique for the quantitative evaluation of the nanoplatelets orientation in ensemble.

Addressing the exciton fine structure in colloidal nanocrystals: the case of CdSe nanoplatelets.

We study the band-edge exciton fine structure and in particular its bright-dark splitting in colloidal semiconductor nanocrystals by four different optical methods based on fluorescence line narrowing and time-resolved measurements at various temperatures down to 2 K. We demonstrate that all these methods provide consistent splitting values and discuss their advances and limitations. Colloidal CdSe nanoplatelets with thicknesses of 3, 4 and 5 monolayers are chosen for experimental demonstrations. The bright-dark splitting of excitons varies from 3.2 to 6.0 meV and is inversely proportional to the nanoplatelet thickness. Good agreement between experimental and theoretically calculated size dependence of the bright-dark exciton splitting is achieved. The recombination rates of the bright and dark excitons and the bright to dark relaxation rate are measured by time-resolved techniques.