ABSTRACT
We describe an optical pump/probe system for sensitive measurements of time-resolved optical measurements of material dynamics. The instrument design is optimized for time-resolved magneto-optic Kerr effect (TR-MOKE) measurements of dynamics in magnetic materials. The system also allows for time-domain thermoreflectance (TDTR) measurements of thermal transport properties and picosecond acoustic measurements of film thickness and/or elastic constants. The system has several advantages over the conventional designs for TR-MOKE and/or TDTR systems. Measurements of pump-induced changes to the probe beam intensity are shot-noise limited. The system's design allows for MOKE and/or thermoreflectance measurements of both sides of a sample. Pumping and probing the sample on opposite sides allows nanoscale flash diffusivity measurements of transport properties. The wavelengths of the pump and probe beams are straightforward to tune between 350-525 nm and 690-1050 nm. A tunable wavelength allows for optical resonances in a wide array of materials to be excited and/or probed. Finally, the setup is calibrated to allow for the real and imaginary components of Kerr signals to be separately quantified.
ABSTRACT
We report results of investigation of the phonon and thermal properties of the exfoliated films of layered single crystals of antiferromagnetic FePS3 and MnPS3 semiconductors. Raman spectroscopy was conducted using three different excitation lasers with wavelengths of 325 nm (UV), 488 nm (blue), and 633 nm (red). UV-Raman spectroscopy reveals spectral features which are not detectable via visible Raman light scattering. The thermal conductivity of FePS3 and MnPS3 thin films was measured by two different techniques: the steady-state Raman optothermal and transient time-resolved magneto-optical Kerr effect. The Raman optothermal measurements provided the orientation-average thermal conductivity of FePS3 to be 1.35 ± 0.32 W m-1 K-1 at room temperature. The transient measurements revealed that the through-plane and in-plane thermal conductivity of FePS3 are 0.85 ± 0.15 and 2.7 ± 0.3 W m-1 K-1, respectively. The films of MnPS3 have higher thermal conductivity of 1.1 ± 0.2 W m-1 K-1 through-plane and 6.3 ± 1.7 W m-1 K-1 in-plane. The data obtained by the two techniques are in agreement and reveal strong thermal anisotropy of the films and the dominance of phonon contribution to heat conduction. The obtained results are important for the interpretation of electric switching experiments with antiferromagnetic materials as well as for the proposed applications of the antiferromagnetic semiconductors in spintronic devices.