ABSTRACT
In order to solely rely on renewable and efficient energy sources, reliable energy storage and production systems are required. Hydrogen is considered an ideal solution as it can be produced electrochemically by water electrolysis and renewably while no pollutants are released when consumed. The most common catalysts in electrolyzers are composed of rare and expensive precious group metals. Replacing these materials with Earth-abundant materials is important to make these devices economically viable. Metal organic frameworks are one possible solution. Herein we demonstrate the synthesis and characterization studies of metal benzene-tri-carboxylic acid-based metal-organic frameworks embedded in activated carbon. The conductive composite material was found to be electrocatalytically active for both the oxygen evolution reaction and the hydrogen evolution reaction. Furthermore, several metal organic frameworks sharing the same ligand but with different first-row transition metals (M = Co, Cu, Fe, Mn) were compared, and the trend of their activity is discussed. Cobalt was found to have the highest activity among the studied metal centers, and therefore has the best potential to serve as a bifunctional catalyst for alkaline electrolyzers.
ABSTRACT
In an effort to develop durable, corrosion-resistant catalyst support materials for polymer electrolyte fuel cells, modified polymer-assisted deposition method was used to synthesize tungsten carbide (WC, WC1-x), which was later used as a support material for Pt-based oxygen reduction reaction catalyst, as an alternative for the corrosion-susceptible, carbon supports. The Pt-deposited tungsten carbide's corrosion-resistance, oxygen reduction reaction electrocatalysis, and durability were studied and compared to that of Pt/C. Bulk free carbon was found to be absent from the ceramic matrix which had particle size in the range of 2-25 nm. Tungsten carbide support appears to enhance the oxygen reduction activity on Pt, showing an increase in mass activity (nearly 2-fold at 0.85 V vs RHE) and specific activity (more than 7 times higher), alongside decrease in overpotential, in comparison to Pt/C. A significant increase in durability was also observed with the tungsten carbide-based system.
ABSTRACT
In this article, we collected the most significant and recent data in brief in the field of metal organic frameworks oxygen reduction reaction catalysts, obtained from some of the most recent research papers in the field. We present lists of materials and their key parameters that are relevant to the cathode catalysts in polymer electrolyte membrane fuel cells. All the materials listed in this paper are composed of metal organic frameworks, zeolitic imidazolate frameworks, or their derivatives. These are divided into two main groups: pristine MOFs and MOF-derived materials. The data in this article is a summary of more extensive review (Gonen and Elbaz, 2018) [1].
ABSTRACT
The oxidation level and properties of reduced graphene oxides (rGOs) were fine-tuned using temperature-programmed reductive annealing. rGOs were annealed at different temperatures (from 500 to 1000 °C) in hydrogen to modulate their oxidation levels. The surface of the rGOs was fully characterized using electron paramagnetic resonance backed by Raman, X-ray diffraction, and chemical analysis measurements. These experiments were used to study the changes in the surface of the rGO, its surface functionalities, and its defects as a function of the reduction temperature. In addition, electrochemical measurements to quantify the oxidation level of the rGOs offer a simple tool to correlate the properties of rGOs with their structure. Finally, we explored the effect of different levels of reduction on conductivity, capacitance, and surface reactivity. This research offers simple methodological techniques and routes to control and characterize the oxidation level of bulk quantities of rGO.