ABSTRACT
According to the idea of sustainable development, humanity should make every effort to care for the natural environment along with economic development. Decreasing water resources in the world makes it necessary to take action to reduce the consumption of this resource. This article presents the results of research conducted to improve the use of recyclable materials in line with the circular economy model. The research focused on the development of a technological solution for the recovery of raw materials from galvanic wastewater. The concept of a galvanic wastewater treatment system presented in the article includes wastewater pre-treatment in the ultrafiltration (UF) process and water recovery in the reverse osmosis (RO) process. In addition, the purpose of the work was to manage post-filtration waste (RO retentate) containing high concentrations of zinc in the process of galvanizing metal details. The obtained results indicate that it is possible to reduce the amount of sewage from the galvanizing industry by reusing the recovered water as technical water in the process line. The carried-out model tests of galvanizing confirmed the possibility of using RO retentate for the production of metal parts. The achieved results are a proposal to solve the problem of reducing the impact of galvanic wastewater on the environment and to improve the profitability of existing galvanizing technologies by reducing the consumption of water and raw materials.
ABSTRACT
In this work, we investigated the bioactivity of anodic oxide coatings on Ti-13Nb-13Zr alloy by plasma electrolytic oxidation (PEO) in solutions containing Ca and P. The bioactive properties of the films were determined by immersion in simulated body fluid (SBF), and their biocompatibility was examined using adult human bone marrow derived mesenchymal stem cells (hBMSCs). The oxide layers were characterised based on their surface morphology (SEM, AFM, profilometry) as well as on their chemical and phase compositions (EDX, XRF, XRD, XPS). We report that anodic oxidation of Ti-13Nb-13Zr led to the development of relatively thick anodic oxide films that were enriched in Ca and P in the form of phosphate compounds. Furthermore, the treatment generated rough surfaces with a significant amount of open pores. The surfaces were essentially amorphous, with small amounts of crystalline phases (anatase and rutile) being observed, depending on the PEO process parameters. SBF soaking led to the precipitation of small crystals after one week of experiment. During culturing of hBMSCs on the bioactive Ti-13Nb-13Zr surfaces the differentiation of human mesenchymal stem cells toward osteoblasts was promoted, which indicated a potential of the modified materials to improve implant osseointegration.