ABSTRACT
Flexible transparent electrodes (FTEs) with an embedded metal mesh are considered a promising alternative to traditional indium tin oxide (ITO) due to their excellent photoelectric performance, surface roughness, and mechanical and environmental stability. However, great challenges remain for achieving simple, cost-effective, and environmentally friendly manufacturing of high-performance FTEs with embedded metal mesh. Herein, a maskless, templateless, and plating-free fabrication technique is proposed for FTEs with embedded silver mesh by combining an electric-field-driven (EFD) microscale 3D printing technique and a newly developed hybrid hot-embossing process. The final fabricated FTE exhibits superior optoelectronic properties with a transmittance of 85.79%, a sheet resistance of 0.75 Ω sq-1 , a smooth surface of silver mesh (Ra ≈ 18.8 nm) without any polishing treatment, and remarkable mechanical stability and environmental adaptability with a negligible increase in sheet resistance under diverse cyclic tests and harsh working conditions (1000 bending cycles, 80 adhesion tests, 120 scratch tests, 100 min ultrasonic test, and 72 h chemical attack). The practical viability of this FTE is successfully demonstrated with a flexible transparent heater applied to deicing. The technique proposed offers a promising fabrication strategy with a cost-effective and environmentally friendly process for high-performance FTE.
ABSTRACT
An electric-field-driven (EFD), µ-3D printed, fused polymer technique has been developed for the fabrication of large-area microscale prototype molds using typical polymer materials, including microcrystalline wax (MC-wax), polycaprolactone (PCL), and polymathic methacrylate (PMMA). This work proposes an alternative for large area microscale modes and overcomes the limitation of high cost in the traditional mold manufacturing industry. The EFD principle enables printing of fused polymers materials more than one order of magnitude lower than the nozzle diameter, contributing to the necking effect of the Taylor cone jet, which is the key factor to achieve the microscale manufacturing. Numerical simulation of electric field distribution between the meniscus and substrate was carried out to elucidate the dependence of electric field distribution on the meniscus condition of three types of polymers under printable voltage, and the electrical field parameters for the EFD µ-3D printing were determined. A number of experiments were printed successfully using a large range of viscosity materials, ranging from tens of mPa·s to hundreds of thousands of mPa·s of PCL and PMMA. The differences in parameters of different materials, such as viscosity, tensile properties, and surface energy, were studied to assess their use in different fields. Using proper process parameters and a nozzle with an inner diameter of 200 µm, three different application cases were completed, including a Wax microarray and microchannel with a minimum dot diameter of 20 µm, a PCL mesh structure with a minimum line width of 5 µm, and a PMMA large-area mold with a maximum aspect ratio of 0.8. Results show that the EFD µ-3D printing has the outstanding advantages of high printing resolution and polymer material universality.