ABSTRACT
Flexible nanocomposite thick films consisting of PVA0.7PANi0.3 polymer blend doped with different concentrations of nanoplatelets functionalized Graphene (NPFGx) (where x = 0, 5, 10, 15, 20, and 25 wt.%) were fabricated using the solution cast technique. Scanning electron microscopy (SEM), X-ray diffractometer (XRD), energy dispersive spectroscopy analysis (EDX), and Fourier-transform infrared spectra (FT-IR) were used to study the structure of the samples. The results showed that the ordered structure, its orientation, the PANis' well dispersion, and the electrostatic forces play a significant role in enhancing the interfaces between the polymer blend and the NPFG. Thermogravimetric analyses (TGA) and Thermoelectrical analyses (TE) showed that the PVA-PANi conducts a promised conjugated blend for thermoelectric applications. The introduction of the NPFG contents into the blend increased the TE measurements as the DC electrical conductivity ≈ 0.0114 (S cm-1), power factor ≈ 3.93 × 10-3 (W m-1 K-2), and Z.T. ≈ 8.4 × 10-7, for the 25 wt.% NPFG nanocomposite film. The effect of the polymers' phonon contribution in the thermal conductivity controlling and enhancing the thermal stability of the prepared nanocomposite films.
ABSTRACT
Polyaniline-NiFe2O4 nanocomposites (PANI-NiFe2O4) with different contents of NiFe2O4 (2.5, 5 and 50 wt%) were prepared via in situ chemical oxidation polymerization, while the nanoparticles nickel ferrite were synthesized by sol-gel method. The prepared samples were characterized using some techniques such as Fourier transforms infrared (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). Moreover, the electrical conductivity and optical properties of the nanocomposites were investigated. Pure (PANI) and the composites containing 2.5 and 5 wt% NiFe2O4 showed amorphous structures, while the one with 50 wt% NiFe2O4 showed a spinel crystalline structure. The SEM images of the composites showed different aggregations for the different nickel ferrite contents. FTIR spectra revealed to the formation of some interactions between the PANI macromolecule and the NiFe2O4 nanoparticles, while the thermal analyses indicated an increase in the composites stability for samples with higher NiFe2O4 nanoparticles contents. The electrical conductivity of PANI-NiFe2O4 nanocomposite was found to increase with the rise in NiFe2O4 nanoparticle content, probably due to the polaron/bipolaron formation. The optical absorption experiments illustrate direct transition with an energy band gap of Eg = 1.0 for PANI-NiFe2O4 nanocomposite.