ABSTRACT
Multiple-pulse S-on-1 laser damage experiments were carried out in the bulk of synthetic fused silica at 355 nm and 266 nm. Two beam sizes were used for each wavelength and the pulse duration was 8 ns. The results showed a fatigue effect that is due to cumulative material modifications. The modifications have a long lifetime and the fatigue dynamics are independent of the used beam sizes but differ for the two wavelengths. Based on the fact that, in the context of material-modification induced damage, the damage thresholds for smaller beams are higher than for larger beams, we discuss possible mechanisms of damage initiation.
ABSTRACT
In this work, rapidly grown KH2PO4 (KDP) crystals extracted from the prismatic and the pyramidal growth sectors of crystal boules were analyzed using photoluminescence measurements. From the spectra, we deduced a robust criterion to discriminate between both growth sectors in an unknown KDP plate. Moreover, spatially resolved photoluminescence was shown to enable a local probing of different planes in the bulk of the material leading to accurate and nondestructive three-dimensional mapping of the sector boundary, which is often the weakest point in terms of laser-damage resistance in rapidly grown KDP crystals.
ABSTRACT
This work is dedicated to the study of so-called fatigue effects upon nanosecond laser-induced damage of several crystalline materials and synthetic fused silica irradiated by multiple pulses. The obtained damage probability versus fluence and pulse number data are exploited to determine if the observed fatigue is due to statistics (the more often the material is irradiated, the higher the probability for it to be damaged) or to material modification under irradiation. Whereas 1064 nm irradiation seems to be responsible for statistic behavior, 355 nm irradiation generates material modifications in the case of synthetic fused silica.