Laser-Induced Thermal Decomposition of Uranium Coordination Compounds with Non-oxidic Ligands to Produce Nitride and Carbide Materials.

The production of ceramics from uranium coordination compounds can be achieved through thermal processing if an excess amount of the desired atoms (i.e., C or N), or reactive gaseous products (e.g., methane or nitrogen oxide) is made available to the reactive uranium metal core via decomposition/fragmentation of the surrounding ligand groups. Here, computational thermodynamic approaches were utilized to identify the temperatures necessary to produce uranium metal from some starting compounds─UI4(TMEDA)2, UCl4(TMEDA)2, UCl3(pyridine)x, and UI3(pyridine)4. Experimentally, precursors were irradiated by a laser under various gaseous environments (argon, nitrogen, and methane) creating extreme reaction conditions (i.e., fast heating, high temperature profile >2000 °C, and rapid cooling). Despite the fast dynamics associated with laser irradiation, the central uranium atom reacted with the thermal decomposition products of the ligands yielding uranium ceramics. Residual gas analysis identified vaporized products from the laser irradiation, and the final ceramic products were characterized by powder X-ray diffraction. The composition of the uranium precursor as well as the gaseous environment had a direct impact on the production of the final phases.

Unconventional Pathways to Carbide Phase Synthesis via Thermal Decomposition of UI4(1,4-dioxane)2.

UI4(1,4-dioxane)2 was subjected to laser-based heating─a method that enables localized, fast heating (T > 2000 °C) and rapid cooling under controlled conditions (scan rate, power, atmosphere, etc.)─to understand its thermal decomposition. A predictive computational thermodynamic technique estimated the decomposition temperature of UI4(1,4-dioxane)2 to uranium (U) metal to be 2236 °C, a temperature achievable under laser irradiation. Dictated by the presence of reactive, gaseous byproducts, the thermal decomposition of UI4(1,4-dioxane)2 under furnace conditions up to 600 °C revealed the formation of UO2, UIx, and U(C1-xOx)y, while under laser irradiation, UI4(1,4-dioxane)2 decomposed to UO2, U(C1-xOx)y, UC2-zOz, and UC. Despite the fast dynamics associated with laser irradiation, the central uranium atom reacted with the thermal decomposition products of the ligand (1,4-dioxane = C4H8O2) instead of producing pure U metal. The results highlight the potential to co-develop uranium precursors with specific irradiation procedures to advance nuclear materials research by finding new pathways to produce uranium carbide.