ABSTRACT
This study aims to check the compatibility of a selection of waste and recycled biopolymers for rammed earth applications in order to replace the more common cement-based stabilization. Five formulations of stabilized rammed earth were prepared with different biopolymers: lignin sulfonate, tannin, sheep wool fibers, citrus pomace and grape-seed flour. The microstructure of the different formulations was characterized by investigating the interactions between earth and stabilizers through mercury intrusion porosimetry (MIP), nitrogen soprtion isotherm, powder X-ray diffraction (XRD) and scanning electron microscopy (SEM). The unconfined compressive strength (UCS) was also evaluated for all stabilized specimens. Three out of five biopolymers were considered suitable as rammed earth stabilizers. The use of wool increased the UCS by 6%, probably thanks to the combined effect of the length of the fibers and the roughness of their surfaces, which gives a contribution in binding clay particles higher than citrus and grape-seed flour. Lignin sulfonate and tannin increased the UCS by 38% and 13%, respectively, suggesting the additives' ability to fill pores, coat soil grains and form aggregates; this capability is confirmed by the reduction in the specific surface area and the pore volume in the nano- and micropore zones.
ABSTRACT
Clay-based materials are the most traditional components of buildings. To improve their performance in a sustainable way, agents can be mixed to fired clay acting as a pore-forming factor. However, firing temperatures highly influence their microstructure which is closely linked to a material's final performance as a ceramic block. To highlight the influence of the firing temperature on microstructure, and more specifically on the pore size distribution of clay-based materials, three innovative porous materials were manufactured. These materials were produced by mixing clay and pore-forming agents. They were characterized by optical and scanning electronic microscopy, x-ray diffraction, mercury intrusion and nitrogen adsorption. These techniques allow the phase identification of materials, show sample microstructure and quantify the pore size distribution at different scales. Furthermore, geometric parameters of sample microstructure such as grain diameter and roundness are estimated by using computer software. To conclude, results provide an enlightenment about the influence of material microstructure on the pore size distribution at two firing temperatures. These results can be useful to allow the tune of porous characteristics and, therefore, contribute to the production of more sustainable construction materials.
ABSTRACT
Linear low density polyethylene (LLDPE)/thermal plastic starch (TPS) blend was studied to prepare the biobased nanocomposite material using organoclay nanofil15 (N15) modified by alkilammonium as the reinforced phase. The LLDPE/TPS blend and its nanocomposites were elaborated by melt mixing method at 160 °C for 7 min. And the compounded sample was filmed by blowing method at three different zones of temperature profile which are 160-170-165 °C. The good dispersion of clay in the polymer blend matrix is showed by X-ray diffraction (XRD) and transmission electronic microscopy (TEM), and a semi-exfoliated structure was obtained. The thermal and mechanical properties of materials are enhanced when N15 is added to the mixture. The effect of N15 on morphology and particles size of TPS phase is also investigated. The biodegradation test shows that more than 60% in weight of LLDPE/TPS film is degraded into CO2, H2O, methane and biomass after 5 months in compost soil.