ABSTRACT
In this study, silver birch (Betula pendula) and Scots pine (Pinus sylvestris) wood planks (1000 × 100 × 25 mm) were thermally modified in pilot-scale equipment. Research extended our knowledge of the thermal modification (TM) process in a closed system under nitrogen pressure, as well as how process parameters affect the chemical composition and mechanical strength of wood. Various TM regimes were selected-maximum temperature (150-180 °C), modification time (30-180 min), and initial nitrogen pressure (3-6 bar). Chemical analyses were performed to assess the amount of extractives, lignin, polysaccharides and acetyl group content following the TM process. The mechanical properties of TM wood were characterized using the modulus of rupture (MOR), modulus of elasticity (MOE), and Brinell hardness. The MOR of both studied wood species following TM in nitrogen was reduced, but MOE changes were insignificant. The Brinell hardness of TM birch wood's tangential surface was much higher than that of the radial surface, although Scots pine wood showed the opposite pattern. TM birch and pine wood specimens with the highest mass loss, acetone soluble extractive amount, and the lowest xylan and acetyl group content had the lowest MOR and Brinell hardness.
ABSTRACT
Phenol-formaldehyde (PF) resins with well-established molecular sizes are promising treatment agents for wood bulk protection. However, due to the presence of hydroxyl groups on the periphery, the PF oligomers tend to absorb the water, which can lead to water penetration into the wood. To overcome this drawback different PF pre-polymers have been chemically modified with different long-chain fatty acid chlorides (FAC) via esterification. To obtain the modified PF (M-PF) resins, the PF pre-polymers with average molecular weight (Mw) from 266 to 884 g/mol were esterified with decanoyl, lauroyl, myristoyl, palmitoyl, and stearoyl chloride in pyridine as the reaction medium. Silver birch (Betula pendula) wood specimens (15 × 70 × 150 mm3) were coated with M-PF pre-polymer 5% (w/w) solutions in tetrahydrofuran (THF), and hydrophobic properties of treated birch wood specimens were evaluated using surface contact angle (CA) measurements of water droplets. For all M-PF resin-treated specimens, CA was almost 2-2.5 times higher than for untreated wood (45°) and it remained 80-125° after 60 s. The aging properties of M-PF resin-coated birch wood were analyzed using artificial weathering with ultraviolet (UV) light and combination of both UV and water spray. Results clearly confirm, that the hydrophobic properties of M-PF-treated wood has short-term character and will gradually disappear during long-term application in outdoor conditions.
ABSTRACT
This study investigated the effect of phenol-formaldehyde (PF) resin treatment on the weathering stability and biological durability of birch plywood. Silver birch (Betula pendula) veneers were vacuum-pressure impregnated with four different PF resins with average molecular weights (Mw) of 292 (resin A), 528 (resin B), 703 (resin C), and 884 g/mol (resin D). The aging properties of PF resin modified birch plywood were analyzed using artificial weathering with ultraviolet (UV) light, UV and water spray, and weathering under outdoor conditions. The same combinations of PF-treated plywood specimens were then tested in soil-bed tests to determine their resistance against soft-rot wood decay. It was not possible to compare weathering processes under artificial conditions to processes under outdoor conditions. However, the weathering stability of birch plywood treated with PF resins A, B, and C, scored better than plywood treated with commercial resin D (regardless of solid content concentration [%]). Results from unsterile soil bed tests showed improvements in resistance to soft-rot wood decay compared to untreated plywood and solid wood. Mass loss [%] was lowest for birch plywood specimens treated with resin of highest solid content concentration (resin D, 20%). Provisional durability ratings delivered durability class (DC) ratings of 2-3, considerably improved over untreated solid wood and untreated birch plywood (DC 5).