ABSTRACT
Objectives: This study evaluated the bleaching efficacy of different in-office protocols associated with violet light emitting diode (V-LED), and measured the pulpal temperature rise caused by V-LED with or without gel application. Materials and Methods: Bovine incisors were distributed in 4 groups (n = 10): VL - V-LED; HP - 35% hydrogen peroxide (control); HYB - hybrid protocol, V-LED applied without gel for 10 irradiation cycles followed by V-LED applied with gel for another 10 irradiation cycles; and HPVL - gel and V-LED applied for 20 irradiation cycles. Three bleaching sessions were performed with 7-day intervals. Bleaching efficacy was evaluated with Δ E a b * , ΔE 00 and ΔWID . Data were recorded at baseline, 7, 14, 21 and 70 days. For pulpal temperature rise, thermocouples were placed inside the pulp chamber of human incisors. To determine intrapulpal temperature, the teeth were irradiated with V-LED with or without application of bleaching gel. Color difference data were analyzed by 2-way repeated measures ANOVA and Tukey's test. Pulpal temperature was analyzed by t-test (α = 5%). Results: VL exhibited lower color ( Δ E a b * and ΔE 00) and whiteness changes (ΔWID ) than the other groups. HPVL presented higher color change values than HYB. HYB and HPVL showed not different ΔWID values; and HP showed the highest whiteness changes at all times. There were significant differences comparing ΔT with gel (8.9°C) and without gel application (7.2°C). Conclusions: HPLV was more efficient than HYB. The 2 protocols with VL showed similar results to control. Gel application combined with VL promoted higher pulpal temperature than to the no gel group.
ABSTRACT
The influence of curing mode and shade of resin cements on the color stability of minimum-thickness ceramic veneers after a three-year storage time in distilled water was evaluated in this study. Ninety-six 0.5-mm-thick feldspathic ceramic veneers (Mark II) were luted onto resin composite substrates (Filtek Z350 XT, shade A2E) with two light-cured (NX3 Light-cure and AllCem Veneer) and dual-cured resin cements (NX3 dual-cure and AllCem) in various shades. The specimens were stored in distilled water at 37°C. Color measurements were performed with a spectrophotometer at the following times: 1h and 24h; 7, 30, and 180 days; and 1, 2, and 3 years. Data for color difference (ΔEab) light-cured and dual-cured resin cements were analyzed by two-way ANOVA with repeated measures and Tukey's test (α = 0.05). For the light-cured cements, the ΔEab values were as follows: NX3-Yellow (2.37±1.35) = ACV-A1 (2.40±1.21) = ACV-Trans (2.52±1.46) = ACV-E-Bleach M (2.56±1.42) = NX3-White (2.69±1.49) = NX3-Clear (2.98±1.68). The lowest ΔE values were found for 1 h (0.61±0.36)a, followed by 24 h (1.15±0.55)b and 30 days (2.48±1.11)c. One year, 180 days, and 2 and 3 years presented higher ΔEab values (3.34±0.94, 3.52±1.04, 3.52±0.95 and 3.55±1.14, respectively)d. For the dual-cured cements, the ΔEab values varied as follows: NX3-Clear (2.32±1.24)a = NX3-Yellow (2.37±1.32)a = NX3-White (2.76±1.43)a < AC-Trans (3.77±1.91)b = AC-A3 (4.13±2.11)b < AC-A1 (5.38±2.92)c. Considering time, the lowest ΔEab values were found for 1 h (0.48±0.25)a, followed by 24 h (2.13 ±0.83)b, 30 days (3.54±1.31)c, and 180 days (3,70±1.73)c. The follow-up times of 1 (4.43±2.15)d, 2 (5.02±1.74)e, and 3 years (4.90±2.12)e presented higher ΔEab values. This study demonstrated that light-cured resin cements were less susceptible to color change than dual-cured cements. After 2 years of follow-up, all cements presented ΔEab values above the acceptability threshold.