Functional assessment of four types of disintegrants and their effect on the spironolactone release properties.

Spironolactone is a drug derived from sterols that exhibits an incomplete oral absorption due to its low water solubility and slow dissolution rate. In this study, formulations of spironolactone with four disintegrants named as croscarmellose sodium, crospovidone, sodium starch glycolate and microcrystalline cellulose II (MCCII) were conducted. The effect of those disintegrants on the tensile strength, disintegration time and dissolution rate of spironolactone-based compacts was evaluated using a factorial design with three categorical factors (filler, lubricant, and disintegrant). The swelling values, water uptake and water sorption studies of these disintegrants all suggested that MCCII compacts disintegrate by a wicking mechanism similar to that of crospovidone, whereas a swelling mechanism was dominant for sodium starch glycolate and croscarmellose sodium. The disintegration time of MCCII and sodium starch glycolate remained unchanged with magnesium stearate. However, this lubricant delayed the disintegration time of crospovidone and croscarmellose sodium. MCCII presented the fastest disintegration time independent of the medium and lubricant employed. The water sorption ratio and swelling values determined sodium starch glycolate followed by croscarmellose sodium as the largest swelling materials, whereas crospovidone and MCCII where the least swelling disintegrants. The swelling property of sodium starch glycolate and croscarmellose sodium was strongly affected by the medium pH. The disintegration time of spironolactone compacts was faster when starch was used as a filler due to the formation of soft compacts. In this case, the type of filler employed rather than the disintegrant had a major effect on the disintegration and dissolution times of spironolactone.

Evaluation of several microcrystalline celluloses obtained from agricultural by-products.

Microcrystalline cellulose (MCCI) has been widely used as an excipient for direct compression due to its good flowability, compressibility, and compactibility. In this study, MCCI was obtained from agricultural by-products, such as corn cob, sugar cane bagasse, rice husk, and cotton by pursuing acid hydrolysis, neutralization, clarification, and drying steps. Further, infrared spectroscopy (IR), X-ray diffraction (XRD), optical microscopy, degree of polymerization (DP), and powder and tableting properties were evaluated and compared to those of Avicel PH101, Avicel PH102, and Avicel PH200. Except for the commercial products, all materials showed a DP from 55 to 97. Particles of commercial products and corn cob had an irregular shape, whereas bagasse particles were elongated and thick. Rice and cotton particles exhibited a flake-like and fiber-like shape, respectively. MCCI as obtained from rice husk and cotton was the most densified material, while that produced from corn cob and bagasse was bulky, porous, and more compressible. All products had a moisture content of less than 10% and yields from 7.4% to 60.4%. MCCI as obtained from bagasse was the most porous and compressible material among all materials. This product also showed the best tableting properties along with Avicel products. Likewise, all MCCI products obtained from the above-mentioned sources showed a more rapid disintegration time than that of Avicel products. These materials can be used as a potential source of MCCI in the production of solid dosage forms.