ABSTRACT
The thermal diffusivity of powder bed plays a crucial role in laser powder bed fusion (LPBF) additive manufacturing. The mechanical properties of the parts built by LPBF are immensely influenced by the thermal properties of the powder bed. This study aims to measure the thermal diffusivity of metallic powder, nickel-based super alloy Inconel718 (IN718), in LPBF using laser flash three-layered analysis in a DLF1600 instrument, which incorporates a special powder cell to encapsulate the powdered sample. Measurements were performed at different temperatures. The thermal diffusivity of several reference samples was measured for the purpose of validating the test results, and it was compared to published data for identical measures. It was observed that experimental results for powder samples were smaller than the actual thermal diffusivity of the sample. R software analysis was used to analyze test data in order to obtain powder thermal diffusivity values that were close to the actual values.
ABSTRACT
Laser powder bed fusion (LPBF) additive manufacturing (AM) has been adopted by various industries as a novel manufacturing technology. Powder spreading is a crucial part of the LPBF AM process that defines the quality of the fabricated objects. In this study, the impacts of various input parameters on the spread of powder density and particle distribution during the powder spreading process are investigated using the DEM (discrete element method) simulation tool. The DEM simulations extend over several powder layers and are used to analyze the powder particle packing density variation in different layers and at different points along the longitudinal spreading direction. Additionally, this research covers experimental measurements of the density of the powder packing and the powder particle size distribution on the construction plate.