ABSTRACT
Recently, there has been an increase in the number of studies conducted on the process of developing hydroxyapatite (HA) to use in biocomposites. HA can be derived from natural sources such as bovine bone. The HA usage obtained from green mussel shells in biocomposites in this study will be explored. The research goal is to investigate the composition effect of biomaterials derived from polycaprolactone (PCL), polylactic acid (PLA), as well as HA obtained from green mussel shells with a chemical blending method on mechanical properties and degradation rate. First, 80 mL of chloroform solution was utilized to immerse 16 g of the PLA/PCL mixture with the ratios of 85:15 and 60:40 for 30 min. A magnetic stirrer was used to mix the solution for an additional 30 min at a temperature and speed of 50 °C and 300 rpm. Next, the hydroxyapatite (HA) was added in percentages of 5%, 10%, and 15%, as well as 20% of the PLA/PCL mixture's total weight. It was then stirred for 1 h at 100 rpm at 65 °C to produce a homogeneous mixture of HA and polymer. The biocomposite mixture was then added into a glass mold as per ASTM D790. Following this, biocomposite specimens were tested for their density, biodegradability, and three points of bending in determining the effect of HA and polymer composition on the degradation rate and mechanical properties. According to the findings of this study, increasing the HA and PLA composition yields a rise in the mechanical properties of the biocomposites. However, the biocomposite degradation rate is increasing.
ABSTRACT
The investigation of hybrid, woven, natural fiber-reinforced polymer composites as a substitute reinforcement for fiber polymer composites has recently caught the interest of academics, industry, and researchers. Woven, natural fiber composites have been implemented in many different applications, including parts for automobiles, household items, flooring, aerospace, and ballistic materials. Therefore, this research seeks to establish the thermal and mechanical characteristics of composites made from rattan strips (RS) and glass fiber (GF)-reinforced epoxy resin (ER). Other than that, the impact of layering configurations with respect to the thermal and mechanical characteristics of the RS and GF will be determined. Hand lay-up and a hydraulic press machine produce hybrid, woven RS and GF laminates. The hybrid composite's mechanical properties will be investigated using impact, tensile, and flexural tests. The hybrid woven of the GF/RS/RS/RS/GF composite sequence demonstrated the highest mechanical properties in comparison to other sequences. The increase from one to three layers of RS in the core layer of GF hybrid composites enhanced the flexural, impact, and tensile properties. In addition, the hybridization of rattan and GF is more thermally stable, as recorded by the high decomposition temperature. As a finding of the research, the woven RS and GF hybrid is a potential material for automotive applications such as car bumpers, for example.
ABSTRACT
The manufacturing of materials, in conjunction with green technology, emphasises the need to employ renewable resources to ensure long-term sustainability. Re-exploring renewable elements that can be employed as reinforcing materials in polymer composites has been a major endeavour. The research goal is to determine how well palm kernel cake filler (PKCF) performs in reinforced epoxy composites. In this study, PKCF with 100 mesh was mixed with epoxy resin (ER) in various ratios ranging from 10% to 40% by weight. Hand lay-up with an open mould is proposed as a method for fabricating the specimen test. Surface modification of PKCF with varying concentrations of NaOH (5 wt.% and 10 wt.%) will be contrasted with the untreated samples. Using Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC), the effect of alkaline treatment will be examined. The tensile and maximum flexural strength of the untreated PKCF/ER composite were determined in this work, with a 30 wt.% of PKCF having the highest tensile strength of 31.20 MPa and the highest flexural strength of 39.70 MPa. The tensile and flexural strength were reduced to 22.90 MPa and 30.50 MPa, respectively, when the filler loading was raised to 40 wt.%. A 5 wt.% alkali treatment for 1 h improved the composites' mechanical characteristics. Lastly, an alkali treatment can aid in the resolution of the problem of inadequate matrix and filler interaction. Alkaline treatment is a popular and effective method for reducing the hydroxyl group in fillers and, thus, improving interfacial bonding. Overall, palm kernel cake is a promising material used as a filler in polymer composites.
ABSTRACT
Pineapple leaf fibre (PALF) is one of the natural fibres with the highest tensile strength and cellulose content. This has led to the investigation of the application of short, long, random mats, and unidirectional types as reinforcement agents, but there is limited study on the usage of woven PALF in composites. Therefore, this study aims to investigate the potential of this woven PALF in reinforcing epoxy resin (ER) composite as well as the effect of layering numbers and fibre orientations on the mechanical properties of the product. This involved using hand lay-up and press moulding with a hydraulic machine to produce the composite and specimen test while 2, 3, and 4 layers of woven PALF were used as the layering number parameter. Moreover, the warp and weft direction of the woven PALF were used to simulate the effect of fibre orientation in composites. The findings showed that the 3-layer woven PALF performed better in terms of tensile and flexural properties than the other layers. It was also discovered that the orientation of the composite with warp direction is slightly higher than the weft direction. Furthermore, the scanning electron microscopic (SEM) method was applied to analyse the tensile fracture of the composites and the results showed that the interfacial adhesion of the 3-layer woven PALF successfully transferred the load to the epoxy resin matrix due to its reinforcement role in composites.
ABSTRACT
The braking system is a crucial element in automotive safety. In order for the braking mechanism to function effectively, the brake pads' durability as well as quality are crucial aspects to take into account. A brake pad is a part of a vehicle that holds the wheel rotation so that braking can occur. Asbestos, which is harmful to human health, is a raw material that is recently being widely used as a material mixture for the manufacturing of brake pads. Many efforts have been made by researchers to find other natural alternative materials to replace the use of asbestos. Natural materials that have received much attention and research include coconut fiber, wood powder or flour, bamboo fiber, shell powder, etc. This review paper focuses on analyzing the main parameters that affect brake pad performance. The composition of filler and fiber types of reinforcement for polymer composites is discussed. Previous studies' information on the fabrication and testing of brake pads are also highlighted. Furthermore, the findings of this review can provide researchers and academicians with useful information and points to consider for further research.
ABSTRACT
This study aims to produce and investigate the potential of biodegradable Polylactic Acid (PLA)-based composites mixed with chitosan and Turmeric Essential Oil (TEO) as an anti-microbial biomaterial. PLA has good barrier properties for moisture, so it is suitable for use as a raw material for making packaging and is included in the GRAS (Generally Recognized As Safe). Chitosan is a non-toxic and antibacterial cationic polysaccharide that needs to be improved in its ability to fight microbes. TEO must be added to increase antibacterial properties due to a large number of hydroxyl (-OH) and carbonyl functional groups. The samples were prepared in three different variations: 2 g of chitosan, 0 mL TEO and 0 mL glycerol (Biofilm 1), 3 g of chitosan, 0.3 mL TEO and 0.5 mL of glycerol (Biofilm 2), and 4 g of chitosan, 0.3 of TEO and 0.5 mL of glycerol (Biofilm 3). The final product was characterized by its functional group through Fourier transform infrared (FTIR); the functional groups contained by the addition of TEO are C-H, C=O, O-H, and N-H with the extraction method, and as indicated by the emergence of a wide band at 3503 cm-1, turmeric essential oil interacts with the polymer matrix by creating intermolecular hydrogen bonds between their terminal hydroxyl group and the carbonyl groups of the ester moieties of both PLA and Chitosan. Thermogravimetric analysis (TGA) of PLA as biofilms, the maximum temperature of a biofilm was observed at 315.74 °C in the variation of 4 g chitosan, 0.3 mL TEO, and 0.5 mL glycerol (Biofilm 3). Morphological conditions analyzed under scanning electron microscopy (SEM) showed that the addition of TEO inside the chitosan interlayer bound chitosan molecules to produce solid particles. Chitosan and TEO showed increased anti-bacterial activity in the anti-microbial test. Furthermore, after 12 days of exposure to open areas, the biofilms generated were able to resist S. aureus and E. coli bacteria.
ABSTRACT
Recently, the most critical issue related to the use of natural fibre-reinforced polymer composites (NFRPC) is the degradation properties of composites exposed to the environment. NFRPC's moisture absorption behaviour has adverse effects on the composite's mechanical properties and dimensional stability. The purpose of this study is to analyse the mechanical properties of epoxy composites reinforced by jute-ramie hybridisation. This study also analysed the effect of stacking sequence hybridisation of the jute-ramie composite on water absorption behaviour. A five-layer different type of stacking sequence of single and hybrid jute-ramie is produced with the hand lay-up method. The results obtained from this study found that the mechanical properties and water absorption behaviour of a single jute fibre are lower compared to a single ramie fibre. The hybrid of jute-ramie has been able to increase the performance of composite compared to pure jute composites. The mechanical properties of the hybrid jute-ramie composite show a reduction effect after exposure to an aqueous environment due to the breakdown of fibre matrix interfacial bonding. However, after 28 days of immersion, all types of the stacking sequence's mechanical properties are still higher than that of pure epoxy resin. In conclusion, the appropriate sequence of stacking and selecting the material used are two factors that predominantly affect the mechanical properties and water absorption behaviour. The hybrid composites with the desired and preferable properties can be manufactured using a hand-lay-up technique and used in the various industrial applications.
ABSTRACT
Woven laminated composite has gained researchers' and industry's interest over time due to its impressive mechanical performance compared to unidirectional composites. Nevertheless, the mechanical properties of the woven laminated composite are hard to predict. There are many micromechanical models based on unidirectional composite but limited to the woven laminated composite. The current research work was conducted to evaluate elastic moduli of hybrid jute-ramie woven reinforced unsaturated polyester composites using micromechanical effectiveness unidirectional models, such as ROM, IROM, Halpin-Tsai, and Hirsch, which are based on stiffness. The hybrid jute-ramie laminated composite was fabricated with different layering sizes, and the stacking sequence was completed via hand lay-up with the compression machine. Tensile modulus values for hybrid composites are between those for single jute and single ramie. Obtained p-values less than 0.05 prove the relationship between layering size and tensile modulus. This study showed that several micromechanical models, such as Halpin-Tsai's predicted value of homogenized mechanical properties, were in good agreement with the experimental result. In the case of the hybrid composite, the micromechanical model deviates from the experimental result. Several modifications are required to improve the current existing model. A correlation function was calculated based on the differences between the elastic modulus values determined experimentally and those derived from each micromechanical model calculation.
ABSTRACT
Nanosilica produced from physically-processed white rice husk ash agricultural waste can be incorporated into geopolymer cement-based materials to improve the mechanical and micro performance. This study aimed to investigate the effect of natural nanosilica on the mechanical properties and microstructure of geopolymer cement. It examined the mechanical behavior of geopolymer paste reinforced with 2, 3, and 4 wt% nanosilica. The tests of compressive strength, direct tensile strength, three bending tests, Scanning Electron Microscope-Energy Dispersive X-ray (SEM/EDX), X-ray Diffraction (XRD), and Fourier-transform Infrared Spectroscopy (FTIR) were undertaken to evaluate the effect of nanosilica addition to the geopolymer paste. The addition of 2 wt% nanosilica in the geopolymer paste increased the compressive strength by 22%, flexural strength by 82%, and fracture toughness by 82% but decreased the direct tensile strength by 31%. The microstructure analysis using SEM, XRD, and FTIR showed the formation of calcium alumina-silicate hydrate (C-A-S-H) gel. The SEM images also revealed a compact and cohesive geopolymer matrix, indicating that the mechanical properties of geopolymers with 2 wt% nanosilica were improved. Thus, it is feasible for nanosilica to be used as a binder.