ABSTRACT
Emissions of formaldehyde from wood-based panels, such as plywood, are gaining increased attention due to their carcinogenic impact on human health and detrimental effects on the environment. Plywood, which is primarily bound with a urea-formaldehyde adhesive, releases formaldehyde during hot pressing and gradually over time. Therefore, this study aims to analyze the impact of non-formaldehyde adhesive types on plywood performance. In addition, plywood performance was assessed by comparing Jabon wood (Anthocephalus cadamba Miq) veneer with other Indonesian wood veneers such as Mempisang (Alphonse spp.) and Mahogany (Swietenia mahagoni). To manufacture a three-layer plywood panel, a two-step manufacturing process was devised. The first step involved the use of Jabon veneers treated with citric acid (CA), maleic acid (MA), and molasses (MO), and another step was carried out for various wood veneers such as Jabon, Mempisang, and Mahogany using CA. The performance of plywood was examined using JAS 233:2003. The performance of plywood bonded with CA was better than that of plywood bonded with MA and MO. The Jabon wood veneer resulted in a lower density of plywood than other wood veneers. The water absorption, thickness swelling, modulus of elasticity, and tensile shear strength of plywood from Jabon wood veneer were similar to those of plywood from Mahogany wood veneer and lower than those of Mempisang wood veneer. The ester linkages of plywood bonded with CA were greater than those of plywood bonded with MA and MO because plywood bonded with CA has better performance than plywood bonded with MA and MO.
ABSTRACT
The fibrovascular bundle (FVB) in palm plants consists of fiber and vascular tissue. Geometrically, it is a long fiber that can be used as an oriented board raw material. This research aimed to examine the performance of citric acid-bonded orientation boards from modified FVB salacca frond under NaOH + Na2SO3 treatment and the bonding mechanism between the modified FVB frond and citric acid. The results showed that changes in the chemical composition of FVB have a positive effect on the contact angle and increase the cellulose crystallinity index. Furthermore, the mechanical properties of the oriented board showed that 1% NaOH + 0.2% Na2SO3 with 60 min immersion has a higher value compared to other treatments. The best dimension stability was on a board with the modified FVB of 1% NaOH + 0.2% Na2SO3 with 30 and 60 min immersion. The bonding mechanism evaluated by FTIR spectra also showed that there is a reaction between the hydroxyl group in the modified FVB and the carboxyl group in citric acid. This showed that the modified combination treatment of NaOH+Na2SO3 succeeded in increasing the mechanical properties and dimensional stability of the orientation board from the FVB salacca frond.
ABSTRACT
This study examined the salinity dependence of triterpenoid content and triterpenoid synthase gene expression in mangrove plants, Kandelia candel and Bruguiera gymnorrhiza (Rhizophoraceae) after long-term exposure to salinity and subsequent re-adaptation. Seedlings of the two mangrove species grown in varying salt concentrations for 4 months were divided into two treatment groups and grown for another 4 months, one group continued under the respective saline condition and the other in fresh water for re-adaptation. The total content of triterpenoids increased with increasing salinity in roots and leaves of K. candel, but only in roots in B. gymnorrhiza. This increase was reversed to a variable extent, depending on the species and organ, after transfer to fresh water. In contrast, the total content of phytosterols showed no correlation with salinity throughout the experiment. The increase in total triterpenoids was accompanied by an up-regulation of several triterpenoid synthase genes: KcMS, a multifunctional triterpenoid synthase, in roots and leaves of K. candel and BgLUS, a lupeol synthase, and BgbAS, a ß-amyrin synthase, in roots of B. gymnorrhiza. The expression of root KcCAS, a cycloartenol synthase, which is involved in phytosterol biosynthesis, was not modulated by the salinity conditions but decreased with increasing salinity in leaves, followed by the restoration to the initial level after transfer to fresh water. The concentrations of individual triterpenoids, but not of phytosterols, in the roots positively correlated with the salinity. These results reinforced the importance of triterpenoids in the adaptation of mangroves to withstand salt and/or water stress.