Effects of airborne-particle abrasion, sodium hydroxide anodization, and electrical discharge machining on porcelain adherence to cast commercially pure titanium.

The aim of this study was to determine the effect of airborne-particle abrasion (APA), sodium hydroxide anodization (SHA), and electrical discharge machining (EDM) on cast titanium surfaces and titanium-porcelain adhesion. Ninety titanium specimens were cast with pure titanium and the alpha-case layer was removed. Specimens were randomly divided into three groups. Ten specimens from each group were subjected to APA. SHA was applied to the second subgroups, and the remaining specimens were subjected to the EDM. For the control group, 10 specimens were cast using NiCr alloy and subjected to only APA. Surfaces were examined by using scanning electron microscope and a surface profilometer. Three titanium porcelains were fused on the titanium surfaces, whereas NiCr specimens were covered with conventional porcelain. Titanium-porcelain adhesion was characterized by a 3-point bending test. Statistical analysis showed that the porcelain-metal bond strength of the control group was higher than that of the titanium-porcelain system (p < 0.05). There were no significant differences between the bond strengths of titanium groups (p 0.05), except the bond strengths of Noritake Super Porcelain TI-22 groups on which APA and SHA were applied (p < 0.05). SHA and EDM as surface treatment did not improve titanium-porcelain adhesion when compared to APA.

Effects of sandblasting and electrical discharge machining on porcelain adherence to cast and machined commercially pure titanium.

The aim of this study was to determine the effect of sandblasting and electrical discharge machining (EDM) on cast and machined titanium surfaces and titanium-porcelain adhesion. Twenty machined titanium specimens were prepared by manufacturer (groups 1 and 2). Thirty specimens were prepared with autopolymerizing acrylic resin. Twenty of these specimens (groups 3 and 4) were cast with commercially pure titanium and the alpha-case layer was removed. For control group (group 5), 10 specimens were cast by using NiCr alloy. Groups 2 and 4 were subjected to EDM while groups 1, 3, and 5 were subjected to sandblasting. Surface examinations were made by using a scanning electron microscope (SEM). A low-fusing porcelain was fused on the titanium surfaces, whereas NiCr specimens were covered using a conventional porcelain. Titanium-porcelain adhesion was characterized by a 3-point bending test. Results were analyzed by Kruskal-Wallis and Mann-Whitney U tests. Metal-porcelain interfaces were characterized by SEM. The bond strength of control group was higher than that of the titanium-porcelain system. There was no significant difference between cast and machined titanium groups (p > 0.05). There was no significant difference between EDM and sandblasting processes (p > 0.05). The use of EDM as surface treatment did not improve titanium-porcelain adhesion compared with sandblasting.