Quantitative in Situ Analysis of Ionomer Structure in Fuel Cell Catalytic Layers.

A quantitative in situ investigation of the structure of the catalytic layer of polymer electrolyte membrane fuel cells using material-sensitive and conductive atomic force microscopy is reported. The distribution and size of the ionomer phase at the surface of the catalytic layer is retrieved from adhesion force mappings, measured at high humidity and up to 75 °C. The average ionomer layer thickness varies between 7 and 13 nm for three differently prepared samples, as concluded from the histograms. Evidence of a lamellar structure of the thinner ionomer layers is presented. A significant thinning of the ionomer layers after long-term fuel cell operation is observed.

Nanosized IrO(x)-Ir Catalyst with Relevant Activity for Anodes of Proton Exchange Membrane Electrolysis Produced by a Cost-Effective Procedure.

We have developed a highly active nanostructured iridium catalyst for anodes of proton exchange membrane (PEM) electrolysis. Clusters of nanosized crystallites are obtained by reducing surfactant-stabilized IrCl3 in water-free conditions. The catalyst shows a five-fold higher activity towards oxygen evolution reaction (OER) than commercial Ir-black. The improved kinetics of the catalyst are reflected in the high performance of the PEM electrolyzer (1 mg(Ir) cm(-2)), showing an unparalleled low overpotential and negligible degradation. Our results demonstrate that this enhancement cannot be only attributed to increased surface area, but rather to the ligand effect and low coordinate sites resulting in a high turnover frequency (TOF). The catalyst developed herein sets a benchmark and a strategy for the development of ultra-low loading catalyst layers for PEM electrolysis.

Microscopic analysis of current and mechanical properties of nafion® studied by atomic force microscopy.

The conductivity of fuel cell membranes as well as their mechanical properties at the nanometer scale were characterized using advanced tapping mode atomic force microscopy (AFM) techniques. AFM produces high-resolution images under continuous current flow of the conductive structure at the membrane surface and provides some insight into the bulk conducting network in Nafion membranes. The correlation of conductivity with other mechanical properties, such as adhesion force, deformation and stiffness, were simultaneously measured with the current and provided an indication of subsurface phase separations and phase distribution at the surface of the membrane. The distribution of conductive pores at the surface was identified by the formation of water droplets. A comparison of nanostructure models with high-resolution current images is discussed in detail.