ABSTRACT
By application of a newly designed T-shaped ligand 5-(4-pyridin-4-yl-benzoylamino)isophthalic acid (H2PBAI) to assemble with Zn(II) ions under solvothermal conditions, a novel porous polyhedral metal-organic framework (Zn-PBAI) with pcu topology has been obtained. When treated as a precursor by annealing of Zn-PBAI at various temperatures, porous carbon polyhedra (PCP) were prepared and tested as an anode material for lithium-ion batteries. The results show that PCP carbonized at 1000 °C (PCP-1000) manifest the highest reversible specific capacity of about 1125 mAh g-1 at a current of 500 mA g-1 after 200 cycles, which is supposed to benefit from the large accessible specific area and high electric conductivity. Moreover, PCP-1000 electrode materials also exhibit superior cyclic stability and good rate capacity.
ABSTRACT
By application of newly designed ligand 5-(3-(pyridin-3-yl)benzamido)isophthalic acid (H2PBI) to react with Mn(NO3)2 under solvothermal conditions, a 2-fold interpenetrated Mn-based metal-organic framework (Mn-PBI) with rutile-type topology has been obtained. When treated as a precursor by pyrolysis of Mn-PBI at 500 °C, mesoporous MnO/C-N nanostructures were prepared and treated as an lithium-ion battery anode. The MnO/C-N manifests good capacity of approximately 1085 mAh g-1 after 100 cycles together with superior cyclic stability and remarkable rate capacity, which is supposed to benefit from a large accessible specific area and unique nanostructures. The remarkable performances suggest promising application as an advanced anode material.