ABSTRACT
Despite the widespread application prospect of soybean meal flour (SF) as a non-toxic and renewable wood adhesive, the practical application is limited by its poor mechanical properties and water resistance. In this work, a novel SF-based wood adhesive (CSP) was developed using citric acid (CA) as a modifier, which was further designated to produce plywood on a laboratory scale. Moreover, the effects of the mass ratio of CA/SF, hot-pressing temperature, and hot-pressing time on the bonding properties and water resistance of the resulting plywood were investigated in detail. As a result, under the optimal hot-pressing conditions (180 °C, 5 min), high-performance plywood bonded by CSP (CA/SF = 15/100) adhesive was fabricated, whose dry shear strength, cold-water wet shear strength (20 °C for 24 h), and hot-water wet shear strength (63 °C for 3 h) reached 1.65 MPa, 1.99 MPa, and 1.58 MPa, respectively. Due to the easy preparation process, sustainability, and favorable properties, the proposed fully bio-based CSP wood adhesive has great potential for the large-scale fabrication of eco-friendly wood panels in industry.