ABSTRACT
This study investigated the impact response behaviours of pineapple leaf fibre (PALF)/carbon hybrid laminate composites for different ply orientations and stacking sequences. The laminates were manufactured using a vacuum infusion approach with various stacking sequences and ply orientations classified as symmetric quasi-isotropic, angle-ply symmetric, and cross-ply symmetric. The laminates were analysed using an IMATEK IM10 drop weight impact tester with an increment of 5 J until the samples were perforated. This investigation reveals that the overall impact properties of PALF and carbon as reinforcements were improved by a beneficial hybridised effect. The laminates with an exterior carbon layer can withstand high impact energy levels up to 27.5 J. The laminate with different stacking sequences had a lower energy transfer rate and ruptured at higher impact energy. The laminates with ply orientations of [0°/90°] and [±45°]8 exhibited 10% to 30% better energy absorption than those with ply orientations of [±45°2, 0°/90°2]s and [0°/90°2, ±45°2]s due to energy being readily transferred within the same linear ply orientation. Through visual inspection, delamination was observed to occur at the interfaces of different stacking sequences and ply orientations.
ABSTRACT
This study examined the fatigue behaviour of pineapple leaf fibre/carbon hybrid laminate composites under various stacking sequences. The vacuum infusion technique was used to fabricate the symmetric quasi-isotropic oriented laminates, in which the stacking was varied. The laminate was tested under static and fatigue tensile load according to ASTM D3039-76 and ASTM D3479-96, respectively. Maximum tensile strength and modulus of 119.34 MPa and 6.86 GPa, respectively, were recorded for the laminate with external PALF ply and internal carbon ply oriented at [± 45°2, 0°/90°2]s (PCCP_45090). The fatigue tests showed that PCCP_45090 and CPPC_09045 (with internal PALF ply and external carbon ply oriented at [0°/90°2, ± 45°2]s) exhibited a higher useful life, especially at the high-stress level of the ultimate tensile strength. The normalised stress against the number of cycles showed that the stacking sequences of different ply orientations affected the fatigue behaviour more than the stacking sequences of the material. The laminate stacking sequence significantly affected the hysteresis energy and stiffness evolution. The scanning electron microscopy images showed that the fatigue failure modes included fibre pull-out, fibre breakage, matrix cracking, debonding, and delamination. The study concluded that PCCP_45090 exhibited an outstanding fatigue performance.
ABSTRACT
In this paper, the effects of stacking sequence and ply orientation on the mechanical properties of pineapple leaf fibre (PALF)/carbon hybrid laminate composites were investigated. The hybrid laminates were fabricated using a vacuum infusion technique in which the stacking sequences and ply orientations were varied, which were divided into the categories of cross-ply symmetric, angle-ply symmetric, and symmetric quasi-isotropic. The results of tensile and flexural tests showed that the laminate with interior carbon plies and ply orientation [0°, 90°] exhibited the highest tensile strength (187.67 MPa) and modulus (5.23 GPa). However, the highest flexural strength (289.46 MPa) and modulus (4.82 GPa) were recorded for the laminate with exterior carbon plies and the same ply orientation. The fracture behaviour of the laminates was determined by using scanning electron microscopy, and the results showed that failure usually initiated at the weakest PALF layer. The failure modes included fibre pull-out, fibre breaking, matrix crack, debonding, and delamination.