BACKGROUND/AIM: During the course of effective and long-term treatment with epidermal growth factor receptor-tyrosine kinase inhibitor (EGFR-TKI), some elderly patients might decline further treatment after EGFR-TKI. We conducted a study to try and understand the reasons for this treatment decision. PATIENTS AND METHODS: We analyzed the medical records of all patients diagnosed with non-small-cell lung cancer with EGFR mutations between 2016 and 2021. RESULTS: There were 108 patients who received EGFR-TKIs. Of these, 67 patients responded to TKI. These responding patients were divided into two groups according to whether they received subsequent TKI treatment. At their request, 24 patients (group A) did not receive further anticancer treatment following TKI. The other 43 patients (group B) received anticancer therapy following TKI. Progression-free survival in group A patients was significantly longer (median=18 months, range=1-67 months) than in group B patients. The reasons for not wanting subsequent treatment after TKI were older age, reduced general condition, deterioration of physical comorbid disease and dementia. Dementia was the most common reason for patients over 75 years of age. CONCLUSION: Some elderly patients with well-controlled disease might express their refusal of all subsequent anticancer therapy after TKIs. Medical staff should respond seriously to these requests.
ABSTRACT
The ionic conductivity of Li6Y(BO3)3 (LYBO) was enhanced by the substitution of tetravalent ions (Zr4+ and Ce4+) for Y3+ sites through the formation of vacancies at the Li sites, an increase in compact densification, and an increase in the Li+-ion conduction pathways in the LYBO phase. As a result, the ionic conductivity of Li5.875Y0.875Zr0.1Ce0.025(BO3)3 (ZC-LYBO) reached 1.7 × 10-5 S cm-1 at 27 °C, which was about 5 orders of magnitude higher than that of undoped Li6Y(BO3)3. ZC-LYBO possessed a large electrochemical window and was thermally stable after cosintering with a LiNi1/3Mn1/3Co1/3O2 (NMC) positive electrode. These characteristics facilitated good reversible capacities in all-solid-state batteries for both NMC positive electrodes and graphite negative electrodes via a simple cosintering process.