Ligand & band gap engineering: tailoring the protocol synthesis for achieving high-quality CsPbI3 quantum dots.

Hot-injection has become the most widespread method used for the synthesis of perovskite quantum dots (QDs) with enormous interest for application in optoelectronic devices. However, there are some aspects of the chemistry involved in this synthesis that have not been completely investigated. In this work, we synthesized ultra-high stable CsPbI3 QDs for more than 15 months by controlling two main parameters: synthesis temperature and the concentration of capping ligands. By increasing the capping ligand concentration during the QD synthesis, we were able to grow CsPbI3 in a broad range of temperatures, improving the photophysical properties of QDs by increasing the synthesis temperature. We achieved the maximum photoluminescence quantum yield (PLQY) of 93% for a synthesis conducted at 185 °C, establishing an efficient surface passivation to decrease the density of non-radiative recombination sites. Under these optimized synthesis conditions, deep red LEDs with an External Quantum Efficiency (EQE) higher than 6% were achieved. The performance of these LEDs is higher than that of the reported CsPbI3 QD-LEDs containing standard capping agents, without additional elements or further element exchange. We show that it is possible to produce stable CsPbI3 QDs with high PLQY and red emission beyond the requirement of the Rec. 2020 standards for red color.

Structural and Electrical Investigation of Cobalt-Doped NiOx/Perovskite Interface for Efficient Inverted Solar Cells.

Inorganic hole-transporting materials (HTMs) for stable and cheap inverted perovskite-based solar cells are highly desired. In this context, NiOx, with low synthesis temperature, has been employed. However, the low conductivity and the large number of defects limit the boost of the efficiency. An approach to improve the conductivity is metal doping. In this work, we have synthesized cobalt-doped NiOx nanoparticles containing 0.75, 1, 1.25, 2.5, and 5 mol% cobalt (Co) ions to be used for the inverted planar perovskite solar cells. The best efficiency of the devices utilizing the low temperature-deposited Co-doped NiOx HTM obtained a champion photoconversion efficiency of 16.42%, with 0.75 mol% of doping. Interestingly, we demonstrated that the improvement is not from an increase of the conductivity of the NiOx film, but due to the improvement of the perovskite layer morphology. We observe that the Co-doping raises the interfacial recombination of the device but more importantly improves the perovskite morphology, enlarging grain size and reducing the density of bulk defects and the bulk recombination. In the case of 0.75 mol% of doping, the beneficial effects do not just compensate for the deleterious one but increase performance further. Therefore, 0.75 mol% Co doping results in a significant improvement in the performance of NiOx-based inverted planar perovskite solar cells, and represents a good compromise to synthesize, and deposit, the inorganic material at low temperature, without losing the performance, due to the strong impact on the structural properties of the perovskite. This work highlights the importance of the interface from two different points of view, electrical and structural, recognizing the role of a low doping Co concentration, as a key to improve the inverted perovskite-based solar cells' performance.

Optical Optimization of the TiO2 Mesoporous Layer in Perovskite Solar Cells by the Addition of SiO2 Nanoparticles.

In this work, SiO2 nanoparticles (NPs) were integrated into the mesoporous TiO2 layer of a perovskite solar cell to investigate their effect on cell performance. Different concentrations of SiO2/ethanol have been combined in TiO2/ethanol to prepare pastes for the fabrication of the mesoporous layer with which perovskite solar cells have been fabricated. Addition of SiO2 NPs of 50 and 100 nm sizes produces an enhancement of cell performance mainly because of an improvement of the photocurrent. This increment is in good agreement with the theoretical predictions based on light scattering induced by dielectric SiO2 NPs. The samples using modified scaffolds with NPs also present a significant lower current-potential hysteresis indicating that NP incorporation also affects the ion accumulation at the perovskite interface, providing an additional beneficial effect. The results stress the importance of the appropriated management of the optical properties on further optimization of perovskite solar cell technology.