How heat controls fracture: the thermodynamics of creeping and avalanching cracks.

While of paramount importance in material science, the dynamics of cracks still lacks a complete physical explanation. The transition from their slow creep behavior to a fast propagation regime is a notable key, as it leads to full material failure if the size of a fast avalanche reaches that of the system. We here show that a simple thermodynamics approach can actually account for such complex crack dynamics, and in particular for the non-monotonic force-velocity curves commonly observed in mechanical tests on various materials. We consider a thermally activated failure process that is coupled with the production and the diffusion of heat at the fracture tip. In this framework, the rise in temperature only affects the sub-critical crack dynamics and not the mechanical properties of the material. We show that this description can quantitatively reproduce the rupture of two different polymeric materials (namely, the mode I opening of polymethylmethacrylate (PMMA) plates, and the peeling of pressure sensitive adhesive (PSA) tapes), from the very slow to the very fast fracturing regimes, over seven to nine decades of crack propagation velocities. In particular, the fastest regime is obtained with an increase of temperature of thousands of Kelvins, on the molecular scale around the crack tip. Although surprising, such an extreme temperature is actually consistent with different experimental observations that accompany the fast propagation of cracks, namely, fractoluminescence (i.e., the emission of visible light during rupture) and a complex morphology of post-mortem fracture surfaces, which could be due to the sublimation of bubbles.

Aftershock sequences and seismic-like organization of acoustic events produced by a single propagating crack.

Brittle fractures of inhomogeneous materials like rocks, concrete, or ceramics are of two types: Nominally brittle and driven by the propagation of a single dominant crack or quasi-brittle and resulting from the accumulation of many microcracks. The latter goes along with acoustic noise, whose analysis has revealed that events form aftershock sequences obeying characteristic laws reminiscent of those in seismology. Yet, their origin lacks explanation. Here we show that such a statistical organization is not only specific to the multi-cracking situations of quasi-brittle failure and seismology, but also rules the acoustic events produced by a propagating crack. This simpler situation has permitted us to relate these laws to the overall scale-free distribution of inter-event time and energy and to uncover their selection by the crack speed. These results provide a comprehensive picture of how acoustic events are organized upon material failure in the most fundamental of fracture states: single propagating cracks.