ABSTRACT
Polymer nanocomposites, which combine the advantages of polymers and fillers, are widely used in the field of automobile and aviation. Polyimine (PI) is an emerging thermoset material with remarkable properties, such as malleability, recyclability, and self-healing. Silicon carbide nano-whiskers (SiCw), as a cheap and high-hardness filler material, are chosen to enhance the properties of polyimine matrix. Silicon carbide nano-whisker-reinforced polyimine (PI-SiCw) nanocomposites were successfully fabricated by heat pressing, which was confirmed by FTIR and XPS tests. According to the results of mechanical tests, the mechanical properties of PI-SiCw nanocomposites were obviously improved. For example, with the addition of 0.5% SiCw, bending strength and bending elongation at break can be simultaneously increased by 33% and 148%, respectively. Surprisingly, the impact strength of PI-SiCw nanocomposites with 2% SiCw was increased by 154% compared to the matrix. SEM and EDS tests showed that the evenly distributed SiCw in the polyimine matrix enhanced the mechanical properties of PI-SiCw nanocomposites according to the mechanism of whiskers pulling out and the bridging principle. According to the TGA test results, the PI composites with SiCw retain a higher weight percentage at 800 °C. The reason was the combined effect of the good thermal stability of SiCw and their strong interactions with the PI matrix. As a result, introducing SiCw into the PI matrix imparts a slight improvement in thermal stability. This article presents an avenue of cost-effective research to enhance the mechanical properties of polyimine composites.
ABSTRACT
Inspired by the mineral bridge between hard phase layers of natural nacre, the biomimetic modified silicon carbide nano-whiskers (MSiCw)/graphene oxide sheets (MGO) reinforced polyimine (PI) composites (MSiCw-MGO-PI) were successfully prepared by heat-pressing at room temperature, which confirmed by FTIR, XPS, and XRD tests. According to the results of mechanical tests, the composites with filling weights of MSiCw and MGO, which were found to be 1% and 0.3%, presented tensile strength of 94.27 MPa, which was 32% higher than the matrix. With the additional weights amount of 1%MSiCw and 0.2%MGO, the impact strength of the composites reached 17.46 KJ/m2, which was increased by 81% compared with the matrix. In addition, the reinforcing mechanisms, such as the bridging principle and mechanism of whiskers pulling out, were investigated by analyzing the fracture surface of MSiCw-MGO-PI composites. The results showed that MSiCw and MGO can synergistically improve the mechanical properties of the composites. In addition, the recyclability of the composites valued by the mechanical properties of the composites from regrinding and heat pressing showed that three generations of MSiCw-MGO-PI composites can still maintain high mechanical properties on account of the better dispersion of the reinforcing phases in the matrix from regrinding.