ABSTRACT
Silicone rubber (SR) is a kind of polymer insulation material with excellent performance. With the service life of silicone rubber products reaching the limit, how to dispose of waste silicone rubber is an urgent problem to be solved. In this paper, silicone rubber-modified asphalt binder (SRMA) was prepared by SR and 90# base asphalt binder. The simulated short-term aging and long-term aging tests of SRMA were carried out using the thin film oven aging test (TFOT) and pressure aging vessel test (PAV). The rotary viscosity test and dynamic shear rheological test (DSR) were applied to the rheological properties of SRMA before and after aging. The degradation degree and chemical composition changes of SR were explored by the toluene insoluble matter test, Fourier transform infrared spectroscopy (FTIR), and a Fluorescence microscope (FM). The results demonstrate that SR can significantly affect the aging resistance, fatigue life, and high-temperature stability of SRMA. As the content of SR rose, the elastic component in SRMA increased, leading to a nice performance in stability at high temperatures and fatigue resistance. However, excessive content (14%wt and 16%wt) had a negative influence on the performance of SRMA. So, the optimal content was speculated to be between 12% and 14%. Furthermore, SR and asphalt binder would be aged and degraded together in the aging process, and this phenomenon was more obvious during long-term aging.
ABSTRACT
BACKGROUND AND OBJECTIVE: The conventional valve stents that are cylindrical in shape will become elliptical when implanted in bicuspid aortic valve, thereby reducing the durability of the artificial valve. In this study, a new design of valve stent is presented where valve stents have elliptical cross-section at the annulus and it is expected to have better expandability and circle shape during the interaction between the stent and bicuspid aortic valve, thereby extending the durability of artificial valve. METHODS: Finite element method (FEM) is used to study the mechanical behavior of the novel valve stent in the bicuspid aortic valve. The effects of three matching relationship between the ellipticity of the stents and the ellipticity of the annulus (i.e., the ellipticity of the stent is greater than, equal to and less than the annulus ellipticity, respectively) on the mechanical behavior of stent expansion are studied. In addition, the expansion mechanical behavior of the novel valve stent at different implantation depths is also compared. RESULTS: Results indicate that novel valve stent implantation with elliptical features is superior to conventional circular valve stent. When the novel valve stent ellipticity is less than the annulus ellipticity, the ellipticity of the novel valve stent after implantation is smaller than that of the conventional circular valve stent. This indicated that the novel valve stent has better expandability and post-expansion shape, making artificial valve to have better durability. The risk of paravalvular leak after implantation is lowest when the novel valve stent ellipticity is less than annulus ellipticity. When the novel valve stent ellipticity coincides with annulus ellipticity, the aortic wall is subjected to greatest stress. With the increase of implantation depth, the stress on the novel valve stent decrease. CONCLUSIONS: This study might provide insights for improving stent design for bicuspid aortic valve.