ABSTRACT
As shown recently, the networks of mesoporous high-surface-area silicates and zeolites undergo a deep depolymerization process in glycerol, near 200 degrees C. Within 1 h, X-ray diffraction analysis amorphous gels are obtained. However, some local ordering subsists as demonstrated by a striking similarity between the silicon and aluminum high-resolution solid-state NMR spectra before and after the reaction. The residual organization could be investigated indirectly in studying the recrystallization of these gels in the presence or absence of structure-directing agents. Were this attempt successful, the way should be opened for the synthesis of molecular sieves starting from gels obtained from naturally occurring zeolites. Here, it will be shown that an amorphous gel obtained from HZSM-5 recovers the initial long-range structure of the parent material in a few hours at 85 degrees C in the presence of an aqueous solution of tetrapropyl ammonium (TPA) or NH3. The recrystallization of HY requires the presence of tetramethylammonium, but about 25% of the crystallization is obtained rapidly (approximately = 1 day) at 80 degrees C with ammonia. Hypotheses about the preorganized structural units are presented. The value of the Si-O-Si angle in the silica cluster seems to be of paramount importance.
ABSTRACT
In glycerol, near 200 degrees C, the silicate networks of mesoporous silicates and zeolites undergo a deep depolymerization process. In a few hours, depending on the initial concentration of the solid in glycerol and on the temperature, amorphous gels are obtained. In these gels, a fraction of the Si-O-Si bonds are transformed into Si-O-C. The constitutional aluminum remains bound to the silica network in the gel. The short range ordering is maintained to some extent: the size of the smallest structural unit in gels obtained from zeolites is in the range of the cubic nanometer, nm3.