ABSTRACT
The stress relaxation dynamics of metallic glass Pd40Ni40P20was studied in both supercooled liquid and glassy states. Time-temperature superposition was found in the metastable liquid, implying an invariant shape of the distribution of times involved in the relaxation. Once in the glass state, the distribution of relaxation times broadens as temperature and fictive temperature decrease, eventually leading to a decoupling of the relaxation in two processes. While the slow one keeps a viscous behavior, the fast one shows an anelastic nature and a time scale similar to that of the collective atomic motion measured by x-ray photon correlation spectroscopy (XPCS). These results suggest that the atomic dynamics of metallic glasses, as determined by XPCS at low temperatures in the glass state, can be related to the rearrangements of particles responsible of the macroscopically reversible anelastic behavior.
ABSTRACT
Variable-resolution fluctuation electron microscopy (VR-FEM) data from measurements on amorphous silicon and PdNiP have been obtained at varying experimental conditions. Measurements have been conducted at identical total electron dose and with an identical electron dose normalized to the respective probe size. STEM probes of different sizes have been created by variation of the semi-convergence angle or by defocus. The results show that defocus yields a reduced normalized variance compared to data from probes created by convergence angle variation. Moreover, the trend of the normalized variance upon probe size variation differs between the two methods. Beam coherence, which affects FEM data, has been analyzed theoretically using geometrical optics on a multi-lens setup and linked to the illumination conditions. Fits to several experimental beam profiles support our geometrical optics theory regarding probe coherence. The normalized variance can be further optimized if one determines the optimal exposure time for the nanobeam diffraction patterns.