ABSTRACT
As the sizes of noble metal catalysts, such as platinum, have been successfully minimized, fundamental insights into the electronic properties of metal sub-nanoclusters are increasingly sought for optimizing their catalytic performance. However, it is difficult to rationalize the catalytic activities of metal sub-nanoclusters owing to their more complex electronic structure compared with those of small molecules and bulky solids. In this study, the adsorption of molecular oxygen on a Pt13 sub-nanocluster supported on a graphene layer was analyzed using density functional theory. Unlike bulk Pt, the Pt13 sub-nanocluster has multiple adsorption sites, and the adsorption energy depends strongly on the type of adsorption site. The O2 adsorption energy does not correlate with the transferred charge between O2 and the Pt13 moiety; therefore, to elucidate the differences in the adsorption sites, we propose an original approach for analyzing the electronic structure change in metal sub-nanoclusters caused by molecular adsorption. Our analysis of the integrated local density of state (LDOS) revealed that O2 adsorption on the Pt13 sub-nanocluster has a distinct feature, different from that on a smaller Pt2 cluster or rather a larger Pt slab. The change in the electronic structure of the Pt13 moiety was primarily observed near the Fermi level, different from that of the Pt slab whose DOS was distributed over a wide energy range. Furthermore, the change in the integrated LDOS correlated well with the O2 adsorption energy on the Pt13 sub-nanocluster.
ABSTRACT
We recently found that [Pt17(CO)12(PPh3)8]z (Pt = platinum; CO = carbon monoxide; PPh3 = triphenylphosphine; z = 1+ or 2+) is a Pt nanocluster (Pt NC) that can be synthesized with atomic precision in air. The present study demonstrates that it is possible to prepare a Pt17-supported carbon black (CB) catalyst (Pt17/CB) with 2.1 times higher oxygen reduction reaction (ORR) activity than commercial Pt nanoparticles/CB by the adsorption of [Pt17(CO)12(PPh3)8]z onto CB and subsequent calcination of the catalyst. Density functional theory calculation strongly suggests that the high ORR activity of Pt17/CB originates from the surface Pt atoms that have an electronic structure appropriate for the progress of ORR. These results are expected to provide design guidelines for the fabrication of highly active ORR catalysts using Pt NCs with a diameter of about 1 nm and thereby enabling the use of reduced amounts of Pt in polymer electrolyte fuel cells.