ABSTRACT
Hematite (α-Fe2O3) emerges as an enticing material for visible-light-driven photocatalysis owing to its remarkable stability, low toxicity, and abundance. However, its inherent shortcomings, such as a short hole diffusion length and high recombination rate, hinder its practical application. Recently, oxygen vacancies (Vo) within hematite have been demonstrated to modulate its photocatalytic attributes. The effects of Vo can be broadly categorized into two opposing aspects: (1) acting as electron donors, enhancing carrier conductivity, and improving photocatalytic performance and (2) acting as surface carrier traps, accelerating excited carrier recombination, and deteriorating performance. Critically, the generation rate, distribution, role, and behavior of Vo significantly differ for synthesis methods due to differences in formation mechanisms and oxygen diffusion. This complexity hampers simplified discussions of Vo, necessitating careful investigation and nuanced discussion tailored to the specific method and conditions employed. Among various approaches, hydrothermal synthesis offers a simple and cost-effective route. Here, we demonstrate a hydrothermal synthesis method for Vo introduction to hematite using a carbon source, where variations in the heating rate have not been previously explored in terms of their influence on Vo generation. The analyses revealed that the concentration of Vo was maximized at a heating rate of 16 °C/min, indicative of a high density of surface defects. With regard to photocatalytic performance, elevated heating rates (16 °C/min) fostered the formation of Vo primarily on the hematite surface. The photocatalytic activity was 7.1 times greater than that of the sample prepared at a low heating rate (2 °C/min). These findings highlight the crucial role of surface defects, as opposed to bulk defects, in promoting hematite photocatalysis. Furthermore, the facile control over Vo concentration achievable via manipulating the heating rate underscores the promising potential of this approach for optimizing hematite photocatalysts.
ABSTRACT
For the purpose of developing a novel ablation therapy for oral cancer, the heat generation and transfer properties of a Ti-coated carbon steel rod with 20-mm length and 1.8-mm outer diameter were investigated by means of a high-frequency induction technique at 300 kHz. The heat generation measurement performed using water (15 mL) revealed that the difference of the inclination angles (θ = 0°, 45° and 90°) relative to the magnetic flux direction only slightly affects the heating behavior, exhibiting the overlapped temperature curves during an induction time of 1200 s. These results suggest that the effect of the shape magnetic anisotropy is almost eliminated, being convenient for the precise control of the ablation temperature in clinical use. In the experiments utilizing a tissue-mimicking phantom, the heat transfer concentrically occurred in the lateral direction for both the planar surface and a 10-mm deep cross-section. However, the former exhibited a considerably lower increase in temperature (ΔT), probably due to the effect of heat dissipation to the ambient air. No significant heat transfer was found to occur to the lower side of the inserted Ti-coated carbon steel rod, which is situated in the longitudinal direction.
ABSTRACT
To develop a novel ablation therapy for human solid cancer, the heating properties of a ferromagnetic carbon steel rod and a prototype Ti-coated needle using this carbon steel rod, were investigated in several high-frequency outputs at 300 kHz. In the former, the heating property was drastically different among the three inclination angles (θ = 0°, 45° and 90°) relative to the magnetic flux direction as a result of the shape magnetic anisotropy. However, the effect of the inclination angles was completely eliminated in the latter. It is considered that the complete non-oriented heating property relative to the magnetic flux direction allows the precise control of the ablation temperature during minimally invasive thermotherapy without a lead-wire connected to a fiber-optic thermometer. This newly designed Ti-coated device will be suitable for clinical use combined with its superior biocompatibility for ablation treatments using high-frequency induction heating.
ABSTRACT
Hyperthermia is a minimally invasive approach to cancer treatment, but it is difficult to heat only the tumor without damaging surrounding tissue. To solve this problem, we studied the effectiveness of chemohyperthermia with docetaxel-embedded magnetoliposomes (DMLs) and an applied alternating current (AC) magnetic field. Human MKN45 gastric cancer cells were implanted in the hind limb of Balb-c/nu/nu mice. Various concentrations of docetaxel-embedded DMLs were injected into the tumors and exposed to an AC magnetic field (n = 6, each). For comparison with hyperthermia alone, magnetite-loaded liposome (ML)-injected tumors were exposed to an AC magnetic field. Furthermore, the results of DML without AC treatment and docetaxel diluted into PBS with AC treatment were also compared (n = 10, each). Tumor surface temperature was maintained between 42 and 43 degrees C. Tumor volume was reduced in the DML group with a docetaxel concentration > 56.8 microg/ml, while a docetaxel concentration > 568.5 microg/ml was required for tumor reduction without hyperthermia. Statistically significant differences in tumor volume and survival rate were observed between the DML group exposed to the magnetic field and the other groups. The tumor disappeared in 3 mice in the DML group exposed to the magnetic field; 2 mice survived over 6 months after treatment, whereas all mice of the other groups died by 15 weeks. Histologically, hyperthermia with DML damaged tumor cells and DML diffused homogeneously. To the best of our knowledge, this is the first report to show that hyperthermia using chemotherapeutic agent-embedded magnetoliposomes has an anticancer effect.