Room temperature bio-engineered multifunctional carbonates for CO2 sequestration and valorization.

This contribution reports, for the first time, on an entirely green bio-engineering approach for the biosynthesis of single phase crystalline 1-D nano-scaled calcite CaCO3. This was validated using H2O as the universal solvent and natural extract of Hyphaene thebaica fruit as an effective chelating agent. In this room temperature green process, CaCl2 and CO2 are used as the unique source of Ca and CO3 respectively in view of forming nano-scaled CaCO3 with a significant shape anisotropy and an elevated surface to volume ratio. In terms of novelty, and relatively to the reported scientific and patented literature in relation to the fabrication of CaCO3 by green nano-chemistry, the current cost effective room temperature green process can be singled out as per the following specificities: only water as universal solvent is used, No additional base or acid chemicals for pH control, No additional catalyst, No critical or supercritical CO2 usage conditions, Only natural extract of thebaica as a green effective chelating agent through its phytochemicals and proper enzematic compounds, room Temperature processing, atmospheric pressure processing, Nanoscaled size particles, and Nanoparticles with a significant shape anisotropy (1-D like nanoparticles). Beyond and in addition to the validation of the 1-D synthesis aspect, the bio-engineered CaCO3 exhibited a wide-ranging functionalities in terms of highly reflecting pigment, an effective nanofertilizer as well as a potential binder in cement industry.

Optical properties of biosynthesized nanoscaled Eu2O3 for red luminescence applications.

This contribution reports on the optical properties of biosynthesised Eu2O3 nanoparticles bioengineered for the first time by a green and cost effective method using aqueous fruit extracts of Hyphaene thebaica as an effective chelating and capping agent. The morphological, structural, and optical properties of the samples annealed at 500°C were confirmed by using a high-resolution transmission electron microscope (HR-TEM), x-ray diffraction analysis (XRD), UV-Vis spectrocopy, and photoluminescence spectrometer. The XRD results confirmed the characteristic body-centered cubic (bcc) structure of Eu2O3 nanoparticles with an average size of 20 nm. HR-TEM revealed square type morphology with an average size of ∼6nm. Electron dispersion energy dispersive x-ray spectroscopy spectrum confirmed the elemental single phase nature of pure Eu2O3. Furthuremore, the Fourier transformed infrared spectroscopy revealed the intrinsic characteristic peaks of Eu-O bond stretching vibrations. UV-Vis reflectance proved that Eu2O3 absorbs in a wide range of the solar spectrum from the VUV-UV region with a bandgap of 5.1 eV. The luminescence properties of such cubic structures were characterized by an intense red emission centered at 614 nm. It was observed that the biosynthesized Eu2O3 nanoparticles exhibit an efficient red-luminescence and hence a potential material as red phosphor.