Recent Progress in High-Mobility Organic Transistors: A Reality Check.

Over the past three decades, significant research efforts have focused on improving the charge carrier mobility of organic thin-film transistors (OTFTs). In recent years, a commonly observed nonlinearity in OTFT current-voltage characteristics, known as the "kink" or "double slope," has led to widespread mobility overestimations, contaminating the relevant literature. Here, published data from the past 30 years is reviewed to uncover the extent of the field-effect mobility hype and identify the progress that has actually been achieved in the field of OTFTs. Present carrier-mobility-related challenges are identified, finding that reliable hole and electron mobility values of 20 and 10 cm2 V-1 s-1 , respectively, have yet to be achieved. Based on the analysis, the literature is then reviewed to summarize the concepts behind the success of high-performance p-type polymers, along with the latest understanding of the design criteria that will enable further mobility enhancement in n-type polymers and small molecules, and the reasons why high carrier mobility values have been consistently produced from small molecule/polymer blend semiconductors. Overall, this review brings together important information that aids reliable OTFT data analysis, while providing guidelines for the development of next-generation organic semiconductors.

Alkylated Selenophene-Based Ladder-Type Monomers via a Facile Route for High-Performance Thin-Film Transistor Applications.

We report the synthesis of two new selenophene-containing ladder-type monomers, cyclopentadiselenophene (CPDS) and indacenodiselenophene (IDSe), via a 2-fold and 4-fold Pd-catalyzed coupling with a 1,1-diborylmethane derivative. Copolymers with benzothiadiazole were prepared in high yield by Suzuki polymerization to afford materials which exhibited excellent solubility in a range of nonchlorinated solvents. The CPDS copolymer exhibited a band gap of just 1.18 eV, which is among the lowest reported for donor-acceptor polymers. Thin-film transistors were fabricated using environmentally benign, nonchlorinated solvents, with the CPDS and IDSe copolymers exhibiting hole mobility up to 0.15 and 6.4 cm2 V-1 s-1, respectively. This high performance was achieved without the undesirable peak in mobility often observed at low gate voltages due to parasitic contact resistance.