Effect of the up-front heat treatment of gelatin particles dispersed in calcium phosphate cements on the in vivo material resorption and concomitant bone formation.

Calcium phosphate cements (CPCs), consisting of a mixture of calcium phosphate powders and setting liquid, have been widely used in orthopedic applications. One of the drawbacks of CPCs is their poor resorbability in the living body, which hinders substitution with natural bones. One of the strategies to facilitate the resorption of CPCs is the incorporation of bioresorbable or water-soluble pore-generating particles (porogens), such as gelatin, in the CPC matrices. In spite of numerous reports, however, little is known about the effect of the dissolution/resorption rate of the porogens on concomitant bone regeneration. In the present study, we prepared preset CPCs dispersed with 10 mass% of low-endotoxin gelatin particles 200-500 µm in diameter having different heat-treatment histories, therefore exhibiting different dissolution rate, and then the obtained CPC/gelatin composites were evaluated for in vivo resorption and concomitant in vivo bone formation behaviors. As the results, the dispersion of gelatin particles markedly promoted in vivo resorption of CPC, and enhanced concomitant bone formation, connective tissue formation, osteoblast proliferation, and vascularization. The dissolution/resorption rate was able to be controlled by changing the up-front heat-treatment temperature. In particular, when CPC/gelatin composites were implanted in distal metaphysis of rabbits, the optimum dissolution/resorption was attained by heat-treating gelatin particles at 383 K for 24 h before dispersing in CPC. Quick resorption of calcium phosphate cement and concomitant bone formation by dispersing properly heat-treated with gelatin particles.

[Safety and structural analysis of polymers produced in manufacturing process of alpha-lipoic acid].

Alpha-Lipoic acid has recently been permitted for use in foodstuffs and is contained in tablets and capsules. Although alpha-lipoic acid is synthesized from adipic acid, the safety of polymers produced during the purification and drying processes has been an issue of concern. Hence, we examined the safety profiles of thermally denatured polymer (LAP-A) and ethanol-denatured polymer (LAP-B) produced in the manufacturing process of alpha-lipoic acid. Furthermore, we conducted structural analysis of these polymers by 1H-NMR and FAB-MS spectroscopy. In a consecutive ingestion test, male and female mice ingested diet containing 0.1 and 0.2% LAP-A and -B for 4 weeks. Blood uric acid, potassium and lactate dehydrogenase (LDH) tended to increase without dose-dependency. Relative liver weights were also increased. However, male dogs that were orally administered LAP-B (500 mg/kg) once did not show any abnormalities in blood parameters or general condition. These findings indicate that alpha-lipoic acid polymers are not acutely toxic; however, chronic ingestion of these polymers may affect liver and kidney functions.