ABSTRACT
The conventional dyeing process requires a substantial amount of auxiliaries and water, which leaches hazardous colored effluents to the environment. Herein, a newly developed sustainable spray dyeing system has been proposed for cotton fabric in the presence of reactive dyes, which has the potential to minimize the textile dyeing industries environmental impact in terms of water consumption and save significant energy. The results suggest that fresh dye solution can be mixed with an alkali solution before spray dyeing to avoid the reactive dye hydrolysis phenomenon. After that, drying at 60-100 °C, wet fixation treating for 1-6 min, and combined treatments (wet fixation + drying) were sequentially investigated and then dye fixation percentages were around 63-65%, 52-70%, and above 80%, respectively. Following this, fixation conditions were optimized using L16 orthogonal designs, including wet fixation time, temperature, dye concentration, and pH with four levels where the "larger-the-better" function was selected to maximize the dye fixation rate. Additionally, the color uniformity and wash and rubbing fastnesses were at an acceptable level when both treatments were applied. Finally, the dyes were hydrolyzed after wet fixation, and the hydrolysis percentages were enhanced after the drying process.
ABSTRACT
Herein, we report the fabrication of highly oxidized silver oxide/silver/tin(IV) oxide (HOSBTO or Ag3+-enriched AgO/Ag/SnO2) nanocomposite under a robust oxidative environment created with the use of concentrated nitric acid. Tin(IV) hydroxide nanofluid is added to the reaction mixture as a stabilizer for the Ag3+-enriched silver oxide in the nanocomposite. The formation of Ag nanoparticles in this nanocomposite originates from the decomposition of silver oxides during calcination at 600 °C. For comparison, poorly oxidized silver oxide/silver/tin(IV) oxide (POSBTO with formula AgO/Ag/SnO2) nanocomposite has also been prepared by following the same synthetic procedures, except for the use of concentrated nitric acid. Finally, we studied in detail the anti-pathogenic capabilities of both nanocomposites against four hazardous pathogens, including pathogenic fish bacterium (Stenotrophomonas maltophilia stain EP10), oomycete (Phytophthora cactorum strain P-25), and two different strains of pathogenic strawberry fungus, BRSP08 and BRSP09 (Collectotrichum siamense). The bioassays reveal that the as-prepared HOSBTO and POSBTO nanocomposites exhibit significant inhibitory activities against the tested pathogenic bacterium, oomycete, and fungus in a dose-dependent manner. However, the degree of dose-dependent effectiveness of the two nanocomposites against each pathogen largely varies.