ABSTRACT
Titanium and its alloys are extensively applied in artificial tooth roots because of their excellent corrosion resistance, high specific strength, and low elastic modulus. However, because of their biological inertness, their surface needs to be modified to improve the osteointegration of titanium implants. The preparation of biologically active calcium-phosphorus coatings on the surface of an implant is one effective method for enhancing the likelihood of bone integration. In this study, osteoinductive peptides were extracted from oyster shells by using acetic acid. Two peptide-containing hydroxyapatite (HA) composite coatings were then prepared: one coating was prepared by hydrothermally synthesizing an HA coating in the presence of peptides (HA/P/M), and the other coating was prepared by hydrothermally synthesizing HA and then immersing the hydrothermally synthesized HA in a peptide solution (HA/P/S). Characterization results indicated that the composite HA coatings containing oyster shell-based peptides were successfully prepared on the alkali-treated pure titanium surfaces. The HA/P/M and HA/P/S composite coatings were found to exhibit excellent hydrophilicity. Protein adsorption tests confirmed that the HA/P/M and HA/P/S coatings had an approximately 2.3 times higher concentration of adsorbed proteins than the pure HA coating.
ABSTRACT
Although titanium (Ti) alloys have been widely employed as biomedical materials, they cannot achieve satisfactory osseointegration when implanted in the human body due to their biologically inert nature. Surface modification can enhance both their bioactivity and corrosion resistance. The present study employed a Ti-5Nb-5Mo alloy with a metastable αâ³ phase. This alloy may undergo phase changes after conventional high-temperature heat treatment, which can deteriorate its properties. This study heat-treated the anodized Ti-5Nb-5Mo alloy by using a low-temperature hydrothermal or vapor thermal method to analyze the effects of heat treatment on its apatite induction. The results revealed that the porous nanotube structure on the surface of the alloy was transformed into anatase nanoparticles after hydrothermal or vapor thermal treatment at 150 °C for 6 h. After immersion in simulated body fluid (SBF) for 7 days, the amount of apatite deposited on the surface of the vapor thermal-treated alloy exceeded that on the hydrothermal-treated alloy. Therefore, post-heat treatment of anodized Ti-5Nb-5Mo by using the vapor thermal method can enhance its apatite inductivity without altering its structure.