ABSTRACT
One of the central aims of the field of spintronics is the control of individual electron spins to effectively manage the transmission of quantized data. One well-known mechanism for controlling electronic spin transport is the chiral-induced spin-selectivity (CISS) effect in which a helical nanostructure imparts a preferential spin orientation on the electronic transport. One potential application of the CISS effect is as a transduction pathway between electronic spin and circularly polarized light within nonreciprocal photonic devices. In this work, we identify and quantify the degree of chiral-induced spin-selective electronic transport in helical polyaniline films using magnetoconductive atomic force microscopy (mcAFM). We then induce circularly polarized quantum light emission from CdSe/CdS core/shell quantum dots placed on these films, demonstrating a degree of circular polarization of up to â¼21%. Utilizing time-resolved photoluminescence microscopy, we measure the radiative lifetime difference associated with left- and right-handed circular polarizations of single emitters. These lifetime differences, in combination with Kelvin probe mapping of the variation of surface potential with magnetization of the substrate, help establish an energy level diagram describing the spin-dependent transport pathways that enable the circularly polarized photoluminescence.
ABSTRACT
We demonstrate an important step toward on-chip integration of single-photon sources at room temperature. Excellent photon directionality is achieved with a hybrid metal-dielectric bullseye antenna, while back-excitation is permitted by placement of the emitter in a subwavelength hole positioned at its center. The unique design enables a direct back-excitation and very efficient front coupling of emission either to a low numerical aperture (NA) optics or directly to an optical fiber. To show the versatility of the concept, we fabricate devices containing either a colloidal quantum dot or a nanodiamond containing silicon-vacancy centers, which are accurately positioned using two different nanopositioning methods. Both of these back-excited devices display front collection efficiencies of â¼70% at NAs as low as 0.5. The combination of back-excitation with forward directionality enables direct coupling of the emitted photons into a proximal optical fiber without any coupling optics, thereby facilitating and simplifying future integration.
ABSTRACT
Interlayer excitons (IXs) formed at the interface of van der Waals materials possess various novel properties. In parallel development, strain engineering has emerged as an effective means for creating 2D quantum emitters. Exploring the intersection of these two exciting areas, we use MoS2/WSe2 heterostructure as a model system and demonstrate how strain, defects, and layering can be utilized to create defect-bound IXs capable of bright, robust, and tunable quantum light emission in the technologically important near-infrared spectral range. Our work presents defect-bound IXs as a promising platform for pushing the performance of 2D quantum emitters beyond their current limitations.
ABSTRACT
Quantum light emitters capable of generating single photons with circular polarization and non-classical statistics could enable non-reciprocal single-photon devices and deterministic spin-photon interfaces for quantum networks. To date, the emission of such chiral quantum light relies on the application of intense external magnetic fields, electrical/optical injection of spin-polarized carriers/excitons or coupling with complex photonic metastructures. Here we report the creation of free-space chiral quantum light emitters via the nanoindentation of monolayer WSe2/NiPS3 heterostructures at zero external magnetic field. These quantum light emitters emit with a high degree of circular polarization (0.89) and single-photon purity (95%), independent of pump laser polarization. Scanning diamond nitrogen-vacancy microscopy and temperature-dependent magneto-photoluminescence studies reveal that the chiral quantum light emission arises from magnetic proximity interactions between localized excitons in the WSe2 monolayer and the out-of-plane magnetization of defects in the antiferromagnetic order of NiPS3, both of which are co-localized by strain fields associated with the nanoscale indentations.
ABSTRACT
Transition metal oxides exhibit a plethora of electrical and magnetic properties described by their order parameters. In particular, ferroic orderings offer access to a rich spectrum of fundamental physics phenomena, in addition to a range of technological applications. The heterogeneous integration of ferroelectric and ferromagnetic materials is a fruitful way to design multiferroic oxides. The realization of freestanding heterogeneous membranes of multiferroic oxides is highly desirable. In this study, epitaxial BaTiO3 /La0.7 Sr0.3 MnO3 freestanding bilayer membranes are fabricated using pulsed laser epitaxy. The membrane displays ferroelectricity and ferromagnetism above room temperature accompanying the finite magnetoelectric coupling constant. This study reveals that a freestanding heterostructure can be used to manipulate the structural and emergent properties of the membrane. In the absence of the strain caused by the substrate, the change in orbital occupancy of the magnetic layer leads to the reorientation of the magnetic easy-axis, that is, perpendicular magnetic anisotropy. These results of designing multiferroic oxide membranes open new avenues to integrate such flexible membranes for electronic applications.
ABSTRACT
Focused ion beam implantation is ideally suited for placing defect centers in wide bandgap semiconductors with nanometer spatial resolution. However, the fact that only a few percent of implanted defects can be activated to become efficient single photon emitters prevents this powerful capability to reach its full potential in photonic/electronic integration of quantum defects. Here an industry adaptive scalable technique is demonstrated to deterministically create single defects in commercial grade silicon carbide by performing repeated low ion number implantation and in situ photoluminescence evaluation after each round of implantation. An array of 9 single defects in 13 targeted locations is successfully created-a ≈70% yield which is more than an order of magnitude higher than achieved in a typical single pass ion implantation. The remaining emitters exhibit non-classical photon emission statistics corresponding to the existence of at most two emitters. This approach can be further integrated with other advanced techniques such as in situ annealing and cryogenic operations to extend to other material platforms for various quantum information technologies.
Subject(s)
Electronics , Photons , Feedback , SemiconductorsABSTRACT
Single-walled carbon nanotubes (SWCNTs) with covalent surface defects have been explored recently due to their promise for use in single-photon telecommunication emission and in spintronic applications. The all-atom dynamic evolution of electrostatically bound excitons (the primary electronic excitations) in these systems has only been loosely explored from a theoretical perspective due to the size limitations of these large systems (>500 atoms). In this work, we present computational modeling of nonradiative relaxation in a variety of SWCNT chiralities with single-defect functionalizations. Our excited-state dynamics modeling uses a trajectory surface hopping algorithm accounting for excitonic effects with a configuration interaction approach. We find a strong chirality and defect-composition dependence on the population relaxation (varying over 50-500 fs) between the primary nanotube band gap excitation E11 and the defect-associated, single-photon-emitting E11* state. These simulations give direct insight into the relaxation between the band-edge states and the localized excitonic state, in competition with dynamic trapping/detrapping processes observed in experiment. Engineering fast population decay into the quasi-two-level subsystem with weak coupling to higher-energy states increases the effectiveness and controllability of these quantum light emitters.
ABSTRACT
Atomically thin transition metal dichalcogenides (TMDs), like MoS2with high carrier mobilities and tunable electron dispersions, are unique active material candidates for next generation opto-electronic devices. Previous studies on ion irradiation show great potential applications when applied to two-dimensional (2D) materials, yet have been limited to micron size exfoliated flakes or smaller. To demonstrate the scalability of this method for industrial applications, we report the application of relatively low power (50 keV)4He+ion irradiation towards tuning the optoelectronic properties of an epitaxially grown continuous film of MoS2at the wafer scale, and demonstrate that precise manipulation of atomistic defects can be achieved in TMD films using ion implanters. The effect of4He+ion fluence on the PL and Raman signatures of the irradiated film provides new insights into the type and concentration of defects formed in the MoS2lattice, which are quantified through ion beam analysis. PL and Raman spectroscopy indicate that point defects are generated without causing disruption to the underlying lattice structure of the 2D films and hence, this technique can prove to be an effective way to achieve defect-mediated control over the opto-electronic properties of MoS2and other 2D materials.
ABSTRACT
Incorporating fluorescent quantum defects in the sidewalls of semiconducting single-wall carbon nanotubes (SWCNTs) through chemical reaction is an emerging route to predictably modify nanotube electronic structures and develop advanced photonic functionality. Applications such as room-temperature single-photon emission and high-contrast bio-imaging have been advanced through aryl-functionalized SWCNTs, in which the binding configurations of the aryl group define the energies of the emitting states. However, the chemistry of binding with atomic precision at the single-bond level and tunable control over the binding configurations are yet to be achieved. Here, we explore recently reported photosynthetic protocol and find that it can control chemical binding configurations of quantum defects, which are often referred to as organic color centers, through the spin multiplicity of photoexcited intermediates. Specifically, photoexcited aromatics react with SWCNT sidewalls to undergo a singlet-state pathway in the presence of dissolved oxygen, leading to ortho binding configurations of the aryl group on the nanotube. In contrast, the oxygen-free photoreaction activates previously inaccessible para configurations through a triplet-state mechanism. These experimental results are corroborated by first principles simulations. Such spin-selective photochemistry diversifies SWCNT emission tunability by controlling the morphology of the emitting sites.
ABSTRACT
Akiyama atomic force microscopy probes represent a unique means of combining several of the desirable properties of tuning fork and cantilever probe designs. As a hybridized mechanical resonator, the vibrational characteristics of Akiyama probes result from a complex coupling between the intrinsic vibrational eigenmodes of its constituent tuning fork and bridging cantilever components. Through a combination of finite element analysis modeling and experimental measurements of the thermal vibrations of Akiyama probes we identify a complex series of vibrational eigenmodes and measure their frequencies, quality factors, and spring constants. We then demonstrate the viability of Akiyama probes to perform bimodal multi-frequency force sensing by performing a multimodal measurement of a surface's nanoscale photothermal response using photo-induced force microscopy imaging techniques. Further performing a parametric search over alternative Akiyama probe geometries, we propose two modified probe designs to enhance the capability of Akiyama probes to perform sensitive bimodal multifrequency force sensing measurements.
ABSTRACT
Individual single-walled carbon nanotubes with covalent sidewall defects have emerged as a class of photon sources whose photoluminescence spectra can be tailored by the carbon nanotube chirality and the attached functional group/molecule. Here we present electroluminescence spectroscopy data from single-tube devices based on (7, 5) carbon nanotubes, functionalized with dichlorobenzene molecules, and wired to graphene electrodes. We observe electrically generated, defect-induced emissions that are controllable by electrostatic gating and strongly red-shifted compared to emissions from pristine nanotubes. The defect-induced emissions are assigned to excitonic and trionic recombination processes by correlating electroluminescence excitation maps with electrical transport and photoluminescence data. At cryogenic conditions, additional gate-dependent emission lines appear, which are assigned to phonon-assisted hot-exciton electroluminescence from quasi-levels. Similar results were obtained with functionalized (6, 5) nanotubes. We also compare functionalized (7, 5) electroluminescence data with photoluminescence of pristine and functionalized (7, 5) nanotubes redox-doped using gold(III) chloride solution. This work shows that electroluminescence excitation is selective toward neutral defect-state configurations with the lowest transition energy, which in combination with gate-control over neutral versus charged defect-state emission leads to high spectral purity.
ABSTRACT
Excitons are often given negative connotation in solar energy harvesting in part due to their presumed short diffusion lengths. We investigate exciton transport in single-crystal methylammonium lead tribromide (MAPbBr3) microribbons via spectrally, spatially, and temporally resolved photocurrent and photoluminescence measurements. Distinct peaks in the photocurrent spectra unambiguously confirm exciton formation and allow for accurate extraction of the low temperature exciton binding energy (39 meV). Photocurrent decays within a few µm at room temperature, while a gate-tunable long-range photocurrent component appears at lower temperatures (about 100 µm below 140 K). Carrier lifetimes of 1.2 µs or shorter exclude the possibility of the long decay length arising from slow trapped-carrier hopping. Free carrier diffusion is also an unlikely source of the highly nonlocal photocurrent, due to their small fraction at low temperatures. We attribute the long-distance transport to high-mobility excitons, which may open up new opportunities for novel exciton-based photovoltaic applications.
ABSTRACT
Developments in the field of nanoplasmonics have the potential to advance applications from information processing and telecommunications to light-based sensing. Traditionally, nanoscale noble metals such as gold and silver have been used to achieve the targeted enhancements in light-matter interactions that result from the presence of localized surface plasmons (LSPs). However, interest has recently shifted to intrinsically doped semiconductor nanocrystals (NCs) for their ability to display LSP resonances (LSPRs) over a much broader spectral range, including the infrared (IR). Among semiconducting plasmonic NCs, spinel metal oxides (sp-MOs) are an emerging class of materials with distinct advantages in accessing the telecommunications bands in the IR and affording useful environmental stability. Here, we report the plasmonic properties of Fe3O4 sp-MO NCs, known previously only for their magnetic functionality, and demonstrate their ability to modify the light-emission properties of telecom-emitting quantum dots (QDs). We establish the synthetic conditions for tuning sp-MO NC size, composition and doping characteristics, resulting in unprecedented tunability of electronic behavior and plasmonic response over 450 nm. In particular, with diameter-dependent variations in free-electron concentration across the Fe3O4 NC series, we introduce a strong NC size dependency onto the optical response. In addition, our observation of plasmonics-enhanced decay rates from telecom-emitting QDs reveals Purcell enhancement factors for simple plasmonic-spacer-emitter sandwich structures up to 51-fold, which are comparable to values achieved previously only for emitters in the visible range coupled with conventional noble metal NCs.
ABSTRACT
Quantum emitters (QEs) in two-dimensional transition metal dichalcogenides (2D TMDCs) have advanced to the forefront of quantum communication and transduction research. To date, QEs capable of operating in O-C telecommunication bands have not been demonstrated in TMDCs. Here we report site-controlled creation of telecom QEs emitting over the 1080 to 1550 nm telecommunication wavelength range via coupling of 2D molybdenum ditelluride (MoTe2) to strain inducing nano-pillar arrays. Hanbury Brown and Twiss experiments conducted at 10 K reveal clear photon antibunching with 90% single-photon purity. The photon antibunching can be observed up to liquid nitrogen temperature (77 K). Polarization analysis further reveals that while some QEs display cross-linearly polarized doublets with ~1 meV splitting resulting from the strain induced anisotropic exchange interaction, valley degeneracy is preserved in other QEs. Valley Zeeman splitting as well as restoring of valley symmetry in cross-polarized doublets are observed under 8 T magnetic field.
ABSTRACT
Solid-state single-photon sources are essential building blocks for quantum photonics and quantum information technologies. This study demonstrates promising single-photon emission from quantum defects generated in single-wall carbon nanotubes (SWCNTs) by covalent reaction with guanine nucleotides in their single-stranded DNA coatings. Low-temperature photoluminescence spectroscopy and photon-correlation measurements on individual guanine-functionalized SWCNTs (GF-SWCNTs) indicate that multiple, closely spaced guanine defect sites within a single ssDNA strand collectively form an exciton trapping potential that supports a localized quantum state capable of room-temperature single-photon emission. In addition, exciton traps from adjacent ssDNA strands are weakly coupled to give cross-correlations between their separate photon emissions. Theoretical modeling identifies coupling mechanism as a capture of band-edge excitons. Because the spatial pattern of nanotube functionalization sites can be readily controlled by selecting ssDNA base sequences, GF-SWCNTs should become a versatile family of quantum light emitters with engineered properties.
Subject(s)
Nanotubes, Carbon , DNA , DNA, Single-Stranded , Optics and Photonics , PhotonsABSTRACT
A low-temperature polarization-resolved magneto-photoluminescence experiment is performed on individual PbS/CdS core/shell quantum dots (QDs). The experiment enables a direct measurement of the exciton Landé g factor and the anisotropic zero-field splitting of the lowest emissive bright exciton triplet in PbS/CdS QDs. While anisotropic splittings of individual QDs distribute randomly in 104-325 µeV range, the exciton Landé g factors increase from 0.95 to 2.70 as the emission energy of the QD increases from 1.0 to 1.2 eV. The tight-binding calculations allow to rationalize these trends as a direct consequence of reducing a cubic symmetry of QD via addition/removal of a few (<70) atoms from the surfaces of the PbS core. Furthermore, it is observed that while right (σâ + ) and left (σâ - ) circularly polarized photoluminescence (PL) peaks split linearly with magnetic field as expected for Zeeman effect, the energy splitting between X and Y linearly polarized PL peaks remains nearly unchanged. The theoretical study reveals rich and complex magnetic field-induced interplay of bright triplet and dark exciton states explaining this puzzling behavior. These findings fill the missing gaps in the understanding of lead salt QDs and provide foundation for development of classical and quantum light sources operating at telecommunication wavelengths.
ABSTRACT
Chemical reactions between semiconducting single-wall carbon nanotubes (SWCNTs) and single-stranded DNA (ssDNA) achieve spatially patterned covalent functionalization sites and create coupled fluorescent quantum defects on the nanotube surface, tailoring SWCNT photophysics for applications such as single-photon emitters in quantum information technologies. The evaluation of relaxation dynamics of photoluminescence (PL) from those coupled quantum defects is essential for understanding the nanotube electronic structure and beneficial to the design of quantum light emitters. Here, we measured the PL decay for ssDNA-functionalized SWCNTs as a function of the guanine content of the ssDNA oligo that dictates the red-shifting of their PL emission peaks relative to the band-edge exciton. We then correlate the observed dependence of PL decay dynamics on energy red-shifts to the exciton potential energy landscape, which is modeled using first-principles approaches based upon the morphology of ssDNA-altered SWCNTs obtained by atomic force microscopy (AFM) imaging. Our simulations illustrate that the multiple guanine defects introduced within a single ssDNA strand strongly interact to create a deep exciton trapping well, acting as a single hybrid trap. The emission decay from the distinctive trapping potential landscape is found to be biexponential for ssDNA-modified SWCNTs. We attributed the fast time component of the biexponential PL decay to the redistribution of exciton population among the lowest energy bright states and a manifold of dark states emerging from the coupling of multiple guanine defects. The long lifetime component in the biexponential decay, on the other hand, is attributed to the redistribution of exciton population among different exciton trapping sites that arise from the binding of multiple ssDNA strands along the nanotube axis. AFM measurements indicate that those trapping sites are separated on average by â¼8 nm along the nanotube axis.
Subject(s)
Nanotubes, Carbon , DNA , DNA, Single-Stranded , Microscopy, Atomic ForceABSTRACT
We synthesized PbS/CdS core/shell quantum dots (QDs) to have functional single-emitter properties for room-temperature, solid-state operation in the telecom O and S bands. Two shell-growth methods-cation exchange and successive ionic layer adsorption and reaction (SILAR)-were employed to prepare QD heterostructures with shells of 2-16 monolayers. PbS/CdS QDs were sufficiently bright and stable to resolve photoluminescence (PL) spectra representing both bands from single nanocrystals using standard detection methods, and for a QD emitting in the O-band a second-order correlation function showed strong photon antibunching, important steps toward demonstrating the utility of lead chalcogenide QDs as single-photon emitters (SPEs). Irrespective of type, few telecom-SPEs exist that are capable of such room-temperature operation. Access to single-QD spectra enabled a direct assessment of spectral line width, which was â¼70-90 meV compared to much broader ensemble spectra (â¼300 meV). We show inhomogeneous broadening results from dispersity in PbS core sizes that increases dramatically with extended cation exchange. Quantum yields (QYs) are negatively impacted at thick shells (>6 monolayers) and, especially, by SILAR-growth conditions. Time-resolved PL measurements revealed that, with SILAR, initially single-exponential PL-decays transition to biexponential, with opening of nonradiative carrier-recombination channels. Radiative decay times are, overall, longer for core/shell QDs compared to PbS cores, which we demonstrate can be partially attributed to some core/shell sizes occupying a quasi-type II electron-hole localization regime. Finally, we demonstrate that shell engineering and the use of lower laser-excitation powers can afford significantly suppressed blinking and photobleaching. However, dependence on shell thickness comes at a cost of less-than-optimal brightness, with implications for both materials and experimental design.
ABSTRACT
Monolayer transition metal dichalcogenides (TMDCs) are promising materials for next generation optoelectronic devices. The exciton diffusion length is a critical parameter that reflects the quality of exciton transport in monolayer TMDCs and limits the performance of many excitonic devices. Although diffusion lengths of a few hundred nanometers have been reported in the literature for as-exfoliated monolayers, these measurements are convoluted by neutral and charged excitons (trions) that coexist at room temperature due to natural background doping. Untangling the diffusion of neutral excitons and trions is paramount to understand the fundamental limits and potential of new optoelectronic device architectures made possible using TMDCs. In this work, we measure the diffusion lengths of neutral excitons and trions in monolayer MoS2 by tuning the background carrier concentration using a gate voltage and utilizing both steady state and transient spectroscopy. We observe diffusion lengths of 1.5 µm and 300 nm for neutral excitons and trions, respectively, at an optical power density of 0.6 W cm-2.
ABSTRACT
A robust and reliable method for enhancing the photoluminescence (PL) of multilayer MoS2 is demonstrated using an oxygen plasma treatment process followed by laser exposure. Here, the plasma and laser treatments result in an indirect-to-direct band gap transition. The oxygen plasma creates a slight decoupling of the layers and converts some of the MoS2 to MoO3. Subsequent laser irradiation further oxidizes the MoS2 to MoO3, as confirmed via X-ray photoelectron spectroscopy, and results in localized regions of brightly luminescent MoS2 monolayer triangular islands as seen in high-resolution transmission electron microscopy images. The PL lifetimes are found to decrease from 494 to 190 ps after plasma and laser treatment, reflecting the smaller size of the MoS2 grains/regions. Atomic force microscopic imaging shows a 2 nm increase in thickness of the laser-irradiated regions, which provides further evidence of the MoS2 being converted to MoO3.