ABSTRACT
One-dimensional Au nanoparticle arrays encapsulated within freestanding SiO2 nanowires are fabricated by thermal oxidation of Au-coated Si nanowires with controlled diameter and surface modulation. The nanoparticle diameter is determined by the Si nanowire diameter and Au film thickness, while the interparticle spacing is independently controlled by the Si nanowire modulation. The optical absorption of randomly oriented Au nanoparticle arrays exhibits a strong plasmonic response at 550 nm. Scanning transmission electron microscopy (STEM)-electron energy loss spectrum (EELS) of nanoparticle arrays confirmed the same plasmonic response and demonstrated uniform optical properties of the Au nanoparticles. The plasmonic response in the STEM-EELS maps is primarily confined around the vicinity of the nanoparticles. On the other hand, examination of the same nanowires by energy-filtered transmission electron microscopy also revealed significant enhancement in the plasmonic excitation in the regions in between the nanoparticles. This versatile route to synthesize one-dimensional Au nanoparticle arrays with independently tailorable nanoparticle diameter and interparticle spacing opens up opportunities to exploit enhanced design flexibility and cost-effectiveness for future plasmonic devices.
ABSTRACT
An ethylene-air laminar diffusion flame successfully provided silicon substrates of anodic aluminum oxide (AAO) template with vertically oriented well-aligned carbon nanotubes. Field emission scanning electron microscopy (SEM) showed that open-tipped carbon nanotubes consisting of tube elements with the same length and diameter uniformly coated the template. High-resolution transmission electron microscopy (TEM) analyses revealed these nanotubes to be multiwalled carbon nanotubes, some well graphitized. It was found that cobalt catalyst particles, but not the porous aluminum templates, helped the growth of carbon nanotubes through graphitization and bonding of carbon nanotubes to the silicon substrates.