Aqueous Sol-Gel Synthesis and Shaping of Covalent Organic Frameworks.

The intrinsic fragility and insoluble nature of covalent organic frameworks (COFs) have strongly impeded their processability for practical applications. Herein, an aqueous-based sol-gel synthetic strategy is reported for the synthesis and shaping of COFs with task-specific applications that satisfy the principles of green chemistry for gram-scale production of crystalline materials. Our successful approach involves three pivotal aspects: the "prodrug mimic" design of water-soluble monomers, the utilization of hydrolyzable bonds, and the manipulation of reaction kinetics. The generality of the method is demonstrated by the successful preparation of representative high-surface area two-dimensional (2D) COFs with several commonly used amines. By virtue of this strategy, a COF colloidal dispersion is achieved and can be formulated into processable fluids, structured films, and COF monoliths. Remarkably, the obtained lightweight (∼0.020 g cm-3) and robust aerogels displayed outstanding adsorption capacity (exceeding 57 times its own weight) toward a variety of organic solvents and exhibited superior thermal insulating properties compared to the widely used sponge and cotton. This work demonstrates a versatile strategy for the synthesis and shaping of processable COF materials in water that will contribute to the development of COF monoliths for advanced applications.

Reprocessible Triketoenamine-Based Vitrimers with Closed-Loop Recyclability.

Development of thermosets that can be repeatedly recycled via both chemical route (closed-loop) and thermo-mechanical process is attractive and remains an imperative task. In this work, we reported a triketoenamine based dynamic covalent network derived from 2,4,6-triformylphloroglucinol and secondary amines. The resulting triketoenamine based network does not have intramolecular hydrogen bonds, thus reducing its π-electron delocalization, lowering the stability of the tautomer structure, and enabling its dynamic feature. By virtue of the highly reversible bond exchange, this novel dynamic covalent bond enables the easy construction of highly crosslinked and chemically reprocessable networks from commercially available monomers. The as-made polymer monoliths exhibit high mechanical properties (tensile strength of 79.4 MPa and Young's modulus of 571.4 MPa) and can undergo a monomer-network-monomer (yields up to 90 %) recycling mediated by an aqueous solution, with the new-generation polymer capable of restoring the material strength to its original state. In addition, owing to its dynamic nature, a catalyst-free and low-temperature reprogrammable covalent adaptable network (vitrimer) was achieved. The design concept reported herein can be applied to the development of other novel vitrimers with high repressibility and recyclability, and sheds light on future design of sustainable polymers with minimal environmental impact.