1.
Int J Biol Macromol ; 251: 126531, 2023 Aug 25.
Article in English | MEDLINE | ID: mdl-37634778

ABSTRACT

Developing a multifunctional biomaterial for bone filling and local antibiotic therapy is a complex challenge for bone tissue engineering. Hybrid nanocomposites of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBHV) with nanohydroxyapatite (nHA), fullerene (C60), and vancomycin (VC) were produced by injection. Fullerene was successfully impregnated with VC, as seen in FTIR. The crystallinity degree of PHBHV was slightly reduced in the presence of C60 and VC (64.3 versus 60.8 %), due to the plasticizing effect of these particles. It also resulted in a decrease in the glass transition temperature (Tg), observed by differential scanning calorimetry (DSC). Dense PHBHV/nHA/C60/VC had a flexural elastic modulus 29 % higher than PHBHV, as a result of the good interface between PHBHV, C60, and nHA - particles of high elastic modulus. Dense disks released 25.03 ± 4.27 % of VC for 14 days, which demonstrated its potential to be an alternative treatment to bone infections. Porous scaffolds of PHBHV/nHA/C60/VC were 3D printed with a porosity of 50 % and porous size of 467 ± 70 µm, and had compression elastic modulus of 0.022 GPa, being a promising material to trabecular bone replacement. The plasticizing effect of C60 improved the printability of the material. The hybrid nanocomposite was non-cytotoxic and showed good ability in adhering macrophage cells.

2.
Polymers (Basel) ; 14(9)2022 May 01.
Article in English | MEDLINE | ID: mdl-35567028

ABSTRACT

Graphene oxide (GO) functionalized curaua fiber (CF) has been shown to improve the mechanical properties and ballistic performance of epoxy matrix (EM) nanocomposites with 30 vol% fiber. However, the possibility of further improvement in the property and performance of nanocomposites with a greater percentage of GO functionalized CF is still a challenging endeavor. In the present work, a novel epoxy composite reinforced with 40 vol% CF coated with 0.1 wt% GO (40GOCF/EM), was subjected to Izod and ballistic impact tests as well as corresponding fractographic analysis in comparison with a GO-free composite (40CF/EM). One important achievement of this work was to determine the characteristics of the GO by means of FE-SEM and TEM. A zeta potential of -21.46 mV disclosed a relatively low stability of the applied GO, which was attributed to more multilayered structures rather than mono- or few-layer flakes. FE-SEM images revealed GO deposition, with thickness around 30 nm, onto the CF. Izod impact-absorbed energy of 813 J/m for the 40GOCF/EM was not only higher than that of 620 J/m for the 40CF/EM but also higher than other values reported for fiber composites in the literature. The GO-functionalized nanocomposite was more optimized for ballistic application against a 7.62 mm projectile, with a lower depth of penetration (24.80 mm) as compared with the 30 vol% GO-functionalized CF/epoxy nanocomposite previously reported (27.43 mm). Fractographic analysis identified five main events in the ballistic-tested 40GOCF/EM composed of multilayered armor: CF rupture, epoxy matrix rupture, CF/matrix delamination, CF fibril split, and capture of ceramic fragments by the CF. Microcracks were associated with the morphological aspects of the CF surface. A brief cost-effective analysis confirmed that 40GOCF/EM may be one of the most promising materials for personal multilayered ballistic armor.