Additive Engineering of the CuSCN Hole Transport Layer for High-Performance Perovskite Semitransparent Solar Cells.

CuSCN has been widely considered a promising candidate for low-cost and high-stable hole transport material in perovskite semitransparent solar cells (STSCs). However, the low conductivity of the solution-processed CuSCN hole transport layer (HTL) hinders the hole extraction and transport in devices, which makes it hard to achieve devices with high performance. Herein, we report a facile additive engineering approach to optimize the p conductivity of CuSCN HTLs in perovskite STSCs. The n-butylammonium iodide additive facilitates the formation of Cu2+ and generates more Cu vacancies in the CuSCN HTL. This realizes a significant enhancement of the hole concentration and p conductivity of the film. Moreover, the additive improves the solubility of the CuSCN precursor solution and results in a uniform coverage on the perovskite active layer. Therefore, the perovskite STSC with a high power conversion efficiency (PCE) of 19.24% has been achieved, which is higher than that of the spiro-OMeTAD (18.83%) and CuSCN (17.45%) counterparts. In addition, the unencapsulated CuSCN-based device retains 87.5% of the initial PCE after 20 days in the ambient atmosphere.

CsPbI2Br Perovskite Solar Cells Based on Carbon Black-Containing Counter Electrodes.

CsPbI2Br perovskite solar cells (PSCs) based on carbon electrodes (CEs) are considered to be low-cost and thermally stable devices. Nevertheless, the insufficient contact and energy level mismatch between the CsPbI2Br layer and CE hinder the further enhancement of the cell efficiency. Herein, a carbon black (CB) interlayer was introduced between the perovskite layer and CE. The hole extraction was facilitated due to the larger contact area and suitable energy band alignment in the CsPbI2Br/CB interface. Further investigation indicated the diffusion of CB nanoparticles from the CE or CB layer to the CsPbI2Br film after a certain period of time. We disclosed the formation of a CB-CsPbI2Br bulk heterojunction structure due to the carbon diffusion, which resulted in an efficiency enhancement. As a result, a record efficiency of 13.13% is achieved for carbon-based inorganic PSCs. This work also reveals that the diffusion of CB nanoparticles in CB-containing PSCs is universal and inevitable, although this kind of diffusion results in the enhancement of cell efficiency.