In situ observation of fracture processes in high-strength concretes and limestone using high-speed X-ray phase-contrast imaging.

The mechanical properties and fracture mechanisms of geomaterials and construction materials such as concrete are reported to be dependent on the loading rates. However, the in situ cracking inside such specimens cannot be visualized using traditional optical imaging methods since the materials are opaque. In this study, the in situ sub-surface failure/damage mechanisms in Cor-Tuf (a reactive powder concrete), a high-strength concrete (HSC) and Indiana limestone under dynamic loading were investigated using high-speed synchrotron X-ray phase-contrast imaging. Dynamic compressive loading was applied using a modified Kolsky bar and fracture images were recorded using a synchronized high-speed synchrotron X-ray imaging set-up. Three-dimensional synchrotron X-ray tomography was also performed to record the microstructure of the specimens before dynamic loading. In the Cor-Tuf and HSC specimens, two different modes of cracking were observed: straight cracking or angular cracking with respect to the direction of loading. In limestone, cracks followed the grain boundaries and voids, ultimately fracturing the specimen. Cracks in HSC were more tortuous than the cracks in Cor-Tuf specimens. The effects of the microstructure on the observed cracking behaviour are discussed.This article is part of the themed issue 'Experimental testing and modelling of brittle materials at high strain rates'.

Deformation field heterogeneity in punch indentation.

Plastic heterogeneity in indentation is fundamental for understanding mechanics of hardness testing and impression-based deformation processing methods. The heterogeneous deformation underlying plane-strain indentation was investigated in plastic loading of copper by a flat punch. Deformation parameters were measured, in situ, by tracking the motion of asperities in high-speed optical imaging. These measurements were coupled with multi-scale analyses of strength, microstructure and crystallographic texture in the vicinity of the indentation. Self-consistency is demonstrated in description of the deformation field using the in situ mechanics-based measurements and post-mortem materials characterization. Salient features of the punch indentation process elucidated include, among others, the presence of a dead-metal zone underneath the indenter, regions of intense strain rate (e.g. slip lines) and extent of the plastic flow field. Perhaps more intriguing are the transitions between shear-type and compression-type deformation modes over the indentation region that were quantified by the high-resolution crystallographic texture measurements. The evolution of the field concomitant to the progress of indentation is discussed and primary differences between the mechanics of indentation for a rigid perfectly plastic material and a strain-hardening material are described.

In situ damage assessment using synchrotron X-rays in materials loaded by a Hopkinson bar.

Split Hopkinson or Kolsky bars are common high-rate characterization tools for dynamic mechanical behaviour of materials. Stress-strain responses averaged over specimen volume are obtained as a function of strain rate. Specimen deformation histories can be monitored by high-speed imaging on the surface. It has not been possible to track the damage initiation and evolution during the dynamic deformation inside specimens except for a few transparent materials. In this study, we integrated Hopkinson compression/tension bars with high-speed X-ray imaging capabilities. The damage history in a dynamically deforming specimen was monitored in situ using synchrotron radiation via X-ray phase contrast imaging. The effectiveness of the novel union between these two powerful techniques, which opens a new angle for data acquisition in dynamic experiments, is demonstrated by a series of dynamic experiments on a variety of material systems, including particle interaction in granular materials, glass impact cracking, single crystal silicon tensile failure and ligament-bone junction damage.

Effect of loading rate on mechanical properties and fracture morphology of spider silk.

Spider silks have been shown to have impressive mechanical properties. In order to assess the effect of extension rate, both quasi-static and high-rate tensile properties were determined for single fibers of major (MA) and minor (MI) ampullate single silk from the orb weaving spider Nephila clavipes . Low rate tests have been performed using a DMA Q800 at 10(-3) s(-1), while high rate analysis was done at 1700 s(-1) utilizing a miniature Kolsky bar apparatus. Rate effects exhibited by both respective silk types are addressed, and direct comparison of the tensile response between the two fibers is made. The fibers showed major increases in toughness at the high extension rate. Mechanical properties of these organic silks are contrasted to currently employed ballistic fibers and examination of fiber fracture mechanisms are probed via scanning electron microscope, revealing a globular rupture surface topography for both rate extremums.