ABSTRACT
Molybdenum disulfide (MoS2) is traditionally grown at a high temperature and subsequently patterned to study its electronic properties or make devices. This method imposes severe limitations on the shape and size of MoS2 crystals that can be patterned precisely at required positions. Here, we describe a method of direct nanoscale patterning of MoS2 at room temperature by exposing a molybdenum thiocubane single-source precursor to a beam of electrons. Molybdenum thiocubanes with various alkylxanthate moieties [Mo4S4(ROCS2)6, where R = alkyl] were prepared using a "self-assembly" approach. Micro-Raman and micro-FTIR spectroscopic studies suggest that exposure to a relatively smaller dose of electrons results in the breakdown of xanthate moieties, leading to the formation of MoS2. High-resolution transmission electron micrographs suggest that the growth of MoS2 most likely happens along (100) planes. An electron-beam-induced chemical transformation of a molybdenum thiocubane resist was exploited to fabricate sub-10 nm MoS2 lines and dense dots as small as 13 nm with a pitch of 33 nm. Since this technique does not require the liftoff and etching steps, patterning of MoS2 with interesting shapes, sizes, and thicknesses potentially leading to tunable band gap is possible.
ABSTRACT
Nanostructures of metal sulfides are conventionally prepared via chemical techniques and patterned using self-assembly. This poses a considerable amount of challenge when arbitrary shapes and sizes of nanostructures are desired to be placed at precise locations. Here, we describe an alternative approach of nanoscale patterning of zinc sulfide (ZnS) directly using a spin-coatable and electron beam sensitive zinc butylxanthate resist without the lift-off or etching step. Time-resolved electron beam damage studies using micro-Raman and micro-FTIR spectroscopies suggest that exposure to a beam of electrons leads to quick disappearance of xanthate moieties most likely via the Chugaev elimination, and further increase of electron dose results in the appearance of ZnS, thereby making the exposed resist insoluble in organic solvents. Formation of ZnS nanocrystals was confirmed by high-resolution transmission electron microscopy and selected area electron diffraction. This property was exploited for the fabrication of ZnS lines as small as 6 nm and also enabled patterning of 10 nm dots with pitches as close as 22 nm. The ZnS patterns fabricated by this technique showed defect-induced photoluminescence related to sub-band-gap optical transitions. This method offers an easy way to generate an ensemble of functional ZnS nanostructures that can be arbitrarily patterned and placed in a precise way. Such an approach may enable programmable design of functional chalcogenide nanostructures.