ABSTRACT
The use of waste from industrial activities is of particular importance for environmental protection. Fly ash has a high potential in the production of construction materials. In the present study, the use of fly ash in the production of geopolymer paste and the effect of Fe2O3, MgO and molarity of NaOH solution on the mechanical strength of geopolymer paste are presented. Samples resulting from the heat treatment of the geopolymer paste were subjected to mechanical tests and SEM, EDS and XRD analyses. Samples were obtained using 6 molar and 8 molar NaOH solution with and without the addition of Fe2O3 and MgO. Samples obtained using a 6 molar NaOH solution where Fe2O3 and MgO were added had higher mechanical strengths compared to the other samples.
ABSTRACT
Crystalline admixtures embedded in concrete may react in the presence of water and generate thin crystals able to fill pores, capillaries and micro-cracks. Once the concrete has dried, the crystalline chemicals sit dormant until another dose of water starts the crystallization again. The research aims to analyses the early age self-sealing effect of a crystalline admixture at a dosage rate of 1-3% of the cement mass. Specimens made with two types of gravel were pre-loaded with three-point bending to up to 90% of the ultimate capacity, and conditioned through wet-dry cycles. Micro-crack closure was measured with a microscope after pre-loading, and after 1 day, 4 days, 8 days, 14 days and 20 days of wet-dry exposure. The results show that an admixture content of 3% achieves the best early self-sealing performance. These results are also confirmed by probabilistic analyses, which also emphasize the self-sealing potential of lower ICW contents.