Ultrathin Y2O3:Eu3+nanodiscs: spectroscopic investigations and evidence for reduced concentration quenching.

Here, we report the synthesis and spectral properties of ultrathin nanodiscs (NDs) of Y2O3:Eu3+. It was found that the NDs of Y2O3:Eu3+ with a thickness of about 1 nm can be fabricated in a reproducible, facile and self-assembling process, which does not depend on the Eu3+ concentration. The thickness and morphology of these NDs were determined with small angle x-ray scattering and transmission electron microscopy. We found that the crystal field in these nanoparticles deviates from both the cubic and monoclinic characteristics, albeit the shape of the 5D0 â†’ 7F J (J = 0, 1, 2) transitions shows some similarity with the transitions in the monoclinic material. The Raman spectra of the non-annealed NDs manifest various vibration modes of the oleic acid molecules, which are used to stabilise the NDs. The annealed NDs show two very weak Raman lines, which may be assigned to vibrational modes of Y2O3 NDs. The concentration quenching of the Eu3+ luminescence of the NDs before annealing is largely suppressed and might be explained in terms of a reduction of the phonon density of states.

Light-emitting nanocasts formed from bio-templates: FESEM and cathodoluminescent imaging studies of butterfly scale replicas.

Nanocasts comprising of red-light-emitting cubic Y(2)O(3):Eu phosphors were made from butterfly wing scale bio-templates. We report herein the first cathodoluminescent images made from such nanocasts and show that valuable insights into the nature of the internal structure of the casts can be gained by the use of this technique. The casts faithfully reproduced the fine sub-micrometre size detail of the scales, as was made evident by both FESEM and cathodoluminescent images that were collected from the same sample areas using a hyphenated FESEM-CL instrument. There was excellent agreement between the FESEM and cathodoluminescent images, the image quality of the latter indicating that the Eu(3+) activator ions were evenly dispersed in the Y(2)O(3):Eu phosphor on a sub-micrometre scale. The casts were made by infilling the natural moulds with a Y(2)O(3):Eu precursor solution that was subsequently dried and fired to convert it into the phosphor material. This method provides a simple, low cost route for fabricating nanostructures having feature dimensions as small as 20 nm in size, and it has the potential to be applied to other metal oxide systems for producing nano-and micro-components for electronic, magnetic or photonic integrated systems.

The role of vaterite and aragonite in the formation of pseudo-biogenic carbonate structures: implications for Martian exobiology.

A simple synthesis of various forms of calcium carbonate with spherical and 'floral' morphologies is reported. Vaterite formation occurs at approximately 25 degrees C, aragonite at approximately 70 degrees C and calcite at about approximately 80 degrees C. These are produced when CO2 is reacted with an aqueous solution of calcium chloride in the presence of ammonia. These conditions may have existed at the surface of Mars in the past, leading us to conclude that such mineral formations may be common there. Although the initial phases are modified over time with changing temperature and pressure conditions, they still influence the final morphology of the carbonates observed. A comparison of these structures with those found in the Martian meteorite ALH84001 suggests, but does not confirm, a non-biogenic origin for the ALH84001 carbonates.