ABSTRACT
The presence of heavy metals often causes significant health risks, particularly cadmium, which is known for its high toxicity. In this study, a glassy carbon electrode was successfully modified by incorporating ZnO-PVA-Graphene nanocomposite, leveraging the excellent electrical properties and electron mobility of the material. Comprehensive material analysis, including XRD, confirmed that ZnO maintained its hexagonal wurtzite crystal structure despite the addition of graphene. Moreover, FESEM analysis showed that increasing graphene concentration led to a reduction in ZnO particle size by 85, 68, and 52 nm, respectively, accompanied by a decrease in band gap energy, as verified by UV-Vis measurements. Photoluminescence tests were also conducted and the result showed a noticeable blue shift in ZnO-PVA-Graphene nanocomposites compared to ZnO-PVA, specifically in the near band-edge (NBE) UV emission within the 374-379 nm wavelength range. Through I-V characterization, the optimal graphene concentration for cadmium detection was identified as 1.5 wt% in ZnO-PVA-Graphene nanocomposites, showing an approximate ohmic response. Meanwhile, square-wave voltammetry analysis of cadmium concentrations ranging from 0 to 80 ppm produced a coefficient of determination of 0.98926 and a Limit of Detection (LOD) of 9.88 ppm. These results showed the significant potential of ZnO-PVA-Graphene nanocomposites as a promising material for further development as an effective electrode modifier, enhancing the sensitivity of detection systems.
ABSTRACT
In this study, we demonstrated the fabrication of the concave conic shape microneedle with the aid of COMSOL Multiphysics simulation. The stress and buckling of the microneedle structure were simulated by applying various loads ranging from 50 to 800 g perpendiculars to the tip in order to predict the occurrence of microneedles structure deformation. The simulation study indicated that the surface buckling deformation does not occur to the microneedle structure with the increment of the load. The microneedles with dimensions of height and diameter tip ranging from 60 to 100 µm and 1 to 4 µm, respectively had been fabricated via an etching process in a mixture of hydrofluoric acid, nitric acid, and acetic acid. Three optimized microneedles but different in the structures were fabricated via the acidic etching process. The reproducibility of 3 different microneedle structures was 15, 20, and 60%, respectively. Stress and buckling analyses of the fabricated microneedles were further carried out on the rat skin. The obtained experimental results show promising applications for the deep dermis, stratum corneum to epidermis layer penetration.