ABSTRACT
Dental clinicians and professionals need an affordable, nontoxic, and effective disinfectant against infectious microorganisms when dealing with the contaminated dental impressions. This study evaluated the efficiency of hypochlorous acid (HOCl) as an antimicrobial disinfectant by spraying technique for the alginate impression materials, compared with sodium hypochlorite, and its effect on dimensional stability and reproduction of details. HOCl with a concentration of 200 ppm for 5 and 10 min was compared with the control group (no treatment) as a negative control and with sodium hypochlorite (% 0.5) as a positive control. Candida albicans, Staphylococcus aureus, and Pseudomonas aeruginosa were selected to assess the antimicrobial activity with the colony forming unit test in addition to the dimensional stability and reproduction of details tests. The results revealed that HOCl had significant antimicrobial activity against all tested microorganisms and experimental time. Interestingly, HOCl showed no impact on the dimensional stability of alginate impression material. HOCl could be an effective antimicrobial agent for alginate impression material without interfering with their surface details and dimensional stability.
ABSTRACT
Objective: This study was conducted to evaluate the influence of the G-CEM ONE adhesive enhancing primer on the shear bond strength of self-adhesive resin cement (G-CEM ONE) to both tooth structure and two different CAD/CAM blocks (GC Initial LiSi and Cerasmart 270). Material and Methods: Forty specimens (cylindrical-shaped, 5 mm in diameter and height) were milled from both CAD/CAM blocks (20 specimens from each block type). Forty sound upper premolars were sectioned to the level of peripheral dentin, then randomly divided into four groups (n = 10): A1: GC Initial LiSi without adhesive enhancing primer; B1: Cerasmart 270 without adhesive enhancing primer; A2: GC Initial LiSi with adhesive enhancing primer; B2: Cerasmart 270 group with adhesive enhancing primer application. The CAD/CAM blocks were cemented on teeth using a self-adhesive resin cement (G-cem one). The shear bond strength was assessed using a computerized universal testing machine. A digital microscope was used to study the mode of failure. The shear bond strength values data were analyzed statistically using paired t-test and independent t-test at the significance level of (0.05). Results: A significant difference was shown in the shear bond strength values among groups (P =0.000). The highest shear bond strength value was revealed in group A2, while group B1 exhibited the lowest shear bond strength value. Conclusion: Using the adhesive enhancing primer on the tooth's surface improved the resin cement's bond strength to CAD/CAM blocks. Additionally, GC Initial LiSi exhibited higher bond strength than Cerasmart 270, with or without the primer (AU)
Objetivo: Este estudo foi conduzido para avaliar a influência do primer adesivo G-CEM ONE na resistência ao cisalhamento do cimento resinoso autoadesivo (G-CEM ONE) tanto na estrutura dentária quanto em dois diferentes blocos CAD/CAM (GC Initial LiSi e Cerasmart 270). Material e Métodos: Quarenta corpos de prova (formato cilíndrico, 5 mm de diâmetro e altura) foram fresados em blocos CAD/CAM (20 corpos de prova de cada tipo de bloco). Quarenta pré-molares superiores sadios foram seccionados até o nível da dentina mais externa e, em seguida, divididos aleatoriamente em quatro grupos (n = 10): A1: GC Initial LiSi sem primer adesivo; B1: Cerasmart 270 sem primer adesivo; A2: GC Initial LiSi com primer adesivo; B2: Grupo Cerasmart 270 com aplicação de primer adesivo. Os blocos CAD/CAM foram cimentados nos dentes com cimento resinoso autoadesivo (G-CEM ONE). A resistência ao cisalhamento foi avaliada utilizando uma máquina de ensaios universal computadorizada. Um microscópio digital foi utilizado para estudar o modo de falha. Os dados dos valores de resistência ao cisalhamento foram analisados estatisticamente por meio do teste t pareado e teste t independente ao nível de significância de (0,05). Resultados: Foi demonstrada diferença significativa nos valores de resistência ao cisalhamento entre os grupos (P =0,000). O maior valor de resistência ao cisalhamento foi revelado no grupo A2, enquanto o grupo B1 exibiu o menor valor de resistência ao cisalhamento. Conclusão:A utilização do primer adesivo na superfície dentária melhorou a resistência de união do cimento resinoso aos blocos CAD/CAM. Além disso, o GC Initial LiSi apresentou maior resistência de união que o Cerasmart 270, com ou sem primer.(AU)