ABSTRACT
Effects of heavy density (rho = 9.2 x 10(3) kg/m(3)) Yb(2)O(3) fine dopant (16 nm in diameter) on the acoustic properties of a high-temperature-vulcanization (HTV) silicone rubber have been investigated, to develop a new acoustic lens material with a low acoustic attenuation (alpha) for the medical array probe application. The HTV silicone rubber has advantages in that it shows a lower alpha than that of a room-temperature-vulcanization (RTV) silicone rubber and it can be mixed by applying shear stress, using roll-milling equipment. Roll-milling time dependence of the HTV silicone rubber indicates that the alpha is closely affected by the dispersion of nanopowders in the rubber matrix. The 8 vol% Yb(2)O(3)-doped HTV silicone rubber mixed for 30 min showed the lowest alpha of 0.73 dB/mm MHz with an acoustic impedance [AI = sound speed (c) x density (rho)] of 1.43 x 10(6) kg/m(2)s at 37 degrees C. Moreover, simulation results reveal that a 5 MHz linear probe using the HTV silicone rubber doped with Yb(2)O(3) powder showed relative sensitivity around 2.6 to 3.0 dB higher than a probe using RTV silicone rubber doped with Yb(2)O(3) powder or SiO2-doped conventional silicone rubber for the ultrasonic medical application.
Subject(s)
Lenses , Silicone Elastomers/chemistry , Transducers , Ultrasonography/instrumentation , Computer-Aided Design , Equipment Design , Equipment Failure Analysis , Reproducibility of Results , Sensitivity and SpecificityABSTRACT
The effects of fine metal oxide particles, particularly those of high-density elements (7.7 to 9.7 x 10(3) kg/m3), on the acoustic properties of silicone rubber have been investigated in order to develop an acoustic lens with a low acoustic attenuation. Silicone rubber doped with Yb2O3 powder having nanoparticle size of 16 nm showed a lower acoustic attenuation than silicone rubber doped with powders of CeO2, Bi2O3, Lu2O3 and HfO2. The silicone rubber doped with Yb2O3 powder showed a sound speed of 0.88 km/s, an acoustic impedance of 1.35 x 10(6) kg/m2s, an acoustic attenuation of 0.93 dB/mmMHz, and a Shore A hardness of 55 at 37 degrees C. Although typical silicone rubber doped with SiO2 (2.6 x 10(3) kg/m3) shows a sound speed of about 1.00 km/s, heavy metal oxide particles decreased the sound velocities to lower than 0.93 km/s. Therefore, an acoustic lens of silicone rubber doped with Yb2O3 powder provides increased sensitivity because it realizes a thinner acoustic lens than is conventionally used due to its low sound speed. Moreover, it has an advantage in that a focus point is not changed when the acoustic lens is pressed to a human body due to its reasonable hardness.