ABSTRACT
Micro/nanosized carbon materials were prepared by electrochemical exfoliation method in the forms of the colloids and thin films. Scanning electronic microscopy, optical and luminescent microscopy, and Raman scattering and luminescent spectroscopy were applied for characterization of materials. The wide photoluminescence band in the visible spectral region was observed for each of the samples. The shape of the photoluminescence band depends on excitation wavelength and on the size of the particles. At least two components with maxima at ~580 and ~710 nm can be distinguished in the photoluminescence spectra. The relations between the photoluminescence properties and morphology of the samples have been described and discussed.
ABSTRACT
The aim of this research is to study the influence of the multi-walled carbon nanotubes (MWCNTs) on the thermomechanical and structural properties of high-density polyethylene. Several, complementary experimental techniques were used, namely, dilatometry, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), Raman spectroscopy, and infrared (IR) spectroscopy. Dilatometry data showed that nanocomposites exhibit anisotropic behavior, and intensity of the anisotropy depends on the MWCNT concentration. The shapes of the dilatometric curves of the nanocomposites under study differ significantly for the radial and longitudinal directions of the samples. DSC results show that MWCNTs weekly influence calorimetry data, while Raman spectra show that the I D/I G ratio decreases when MWCNT concentration increases. The IR spectra demonstrate improvement of the crystallinity of the samples as the content in MWCNTs rises.
ABSTRACT
Nanocomposite materials of the Fe-Cu system with/without small addition of carbon nanotubes have been synthesized by mechanochemical activation of elemental Fe and Cu powders in a high-energy planetary ball mill and have been examined by the X-ray diffraction method, SEM and the thermopower methods; the tensile strength of the materials obtained has been estimated. The metastable (Fe, Cu) supersaturated solid solution is formed in the Fe-Cu nanocomposites during milling process. The coherent scattering block size of the materials obtained is decreased with increase of milling time. The duration of mechanochemical activation affects the physical properties of nanocomposites studied. Addition of a small amount of nanotubes into Fe-Cu charge results in a significant increase of strength of the Fe-Cu (4:1) + CNT nanocomposite materials (NCMs) obtained.
ABSTRACT
The objective of this work is a dilatometric study of Al + 0.1% of multiwall carbon nanotubes nanocomposite material (NCM) in three directions: X - parallel to the rolling direction; Y - perpendicular to the rolling direction and (Z) perpendicular to the ribbon plane. NCM specimens were made in the form of a 0.1-mm-thick ribbon. The temperature range used for measurements was 20°C to 600°C. The obtained results show that presence of nanotubes affects the thermal expansion coefficient (TEC) measured in different directions. αx(T) and αy(T) - TEC plots as a function of temperature along X and Y directions, respectively - have substantially the same shape and overlap in the area of 400°C. The expansion along X-axis becomes greater than along Y-axis below this temperature value. It is clear that the coefficient αz(T) is lower than αx(T) and αy(T) over the entire temperature range. The expansion along Z-axis is smaller compared to that along X- and Y-axes. This behaviour suggests that there is a strong interatomic interaction along this direction (Z). αz(T) becomes monotonous and constant and is equal to 8 × 10(-6)°C(-1) at temperatures above 300°C. Such order of magnitude had not been obtained in earlier studies of aluminium alloys. The obtained TEC shows high anisotropy, which grows with the increase of temperature. The heat flow (differential scanning calorimetry, (DSC)) of Al + 0.1% carbon nanotubes (CNT) NCM is more intense compared to that of pure aluminium produced in similar conditions. The two representative curves have similar shape and are almost entirely overlapped. The thermogravimetry results confirm those of DSC. The Raman spectrum of this nanomaterial shows that intensity of G and D bonds is significantly increased compared to that of the pure material. The infrared diagram also confirms that in this case the mentioned bonds are more intensive NCM. The tensile strength measurements (σB) of the studied NCM also demonstrate that its value increases from 140 ± 10 MPa for Al without nanotubes to 200 ± 10 MPa for NCM.