A titanosilicate molecular sieve with adjustable pores for size-selective adsorption of molecules.

Zeolites and related crystalline microporous oxides-tetrahedrally coordinated atoms covalently linked into a porous framework-are of interest for applications ranging from catalysis to adsorption and ion-exchange. In some of these materials (such as zeolite rho) adsorbates, ion-exchange, and dehydration and cation relocation can induce strong framework deformations. Similar framework flexibility has to date not been seen in mixed octahedral/tetrahedral microporous framework materials, a newer and rapidly expanding class of molecular sieves. Here we show that the framework of the titanium silicate ETS-4, the first member of this class of materials, can be systematically contracted through dehydration at elevated temperatures to 'tune' the effective size of the pores giving access to the interior of the crystal. We show that this so-called 'molecular gate' effect can be used to tailor the adsorption properties of the materials to give size-selective adsorbents suitable for commercially important separations of gas mixtures of molecules with similar size in the 4.0 to 3.0 A range, such as that of N2/CH4, Ar/O2 and N2/O2.

Self-propagating metathesis routes to metastable group 4 phosphides.

Group 4 phosphides, which are typically prepared at high temperatures (> 800 degrees C) over several days, are synthesized in self-propagating metathesis (exchange) reactions in seconds. These reactions produce cubic forms of zirconium phosphide (ZrP) and hafnium phosphide (HfP) which are normally made at temperatures greater than 1425 degrees C and 1600 degrees C, respectively. To test whether the high temperatures reached in the metathesis reactions are responsible for the formation of the cubic phases, inert salts are added to lower the maximum reaction temperatures. The lower temperature reactions still result in cubic phosphides, although smaller crystallites form. Further experiments with phosphorus addition indicate that the phosphorus content is not responsible for cubic phase formation. Templating is ruled out using lattice mismatched KCl and hexagonal ZnS as additives. Therefore, the direct synthesis of the high-temperature cubic phase in metathesis reactions appears to be caused by nucleation of the metastable cubic form that is then trapped by rapid cooling. Heating the cubic phase of either ZrP or HfP to 1000 degrees C for 18 h, or carrying out metathesis reactions in sealed ampules at 1000 degrees C, results only in the hexagonal phase.