Chicken Cartilage-Derived Carbon for Efficient Xylene Removal.

Chicken cartilage was used for the first time as a raw material for the microwave-assisted synthesis of biochar and activated carbon. Various microwave absorbers, i.e., commercial active carbon, scrap tyres, silicon carbide, and chicken bone-derived biochar, as well as various microwave powers, were tested for their effect on the rate of pyrolysis and the type of products formed. Biochars synthesised under 400 W in the presence of scrap tyres and chicken bone-derived biochar were activated with KOH and K2CO3 with detergent to produce activated carbon with a highly developed porous structure that would be able to effectively adsorb xylene vapours. All carbons were thoroughly characterised (infrared spectroscopy, X-ray fluorescence spectrometry, nitrogen adsorption/desorption, Raman spectroscopy, proximate and ultimate analysis) and tested as xylene sorbents in dynamic systems. It was found that the activation causes an increase of up to 1042 m2·g-1 in the specific surface area, which ensures the sorption capacity of xylene about 300 mg·g-1. Studies of the composition of biogas emitted during pyrolysis revealed that particularly valuable gaseous products are formed when pyrolysis is carried out in the presence of silicon carbide as a microwave absorber.

A Case Study of Waste Scrap Tyre-Derived Carbon Black Tested for Nitrogen, Carbon Dioxide, and Cyclohexane Adsorption.

Waste scrap tyres were thermally decomposed at the temperature of 600 °C and heating rate of 10 °C·min-1. Decomposition was followed by the TG analysis. The resulting pyrolytic carbon black was chemically activated by a KOH solution at 800 °C. Activated and non-activated carbon black were investigated using high pressure thermogravimetry, where adsorption isotherms of N2, CO2, and cyclohexane were determined. Isotherms were determined over a wide range of pressure, 0.03-4.5 MPa for N2 and 0.03-2 MPa for CO2. In non-activated carbon black, for the same pressure and temperature, a five times greater gas uptake of CO2 than N2 was determined. Contrary to non-activated carbon black, activated carbon black showed improved textural properties with a well-developed irregular mesoporous-macroporous structure with a significant amount of micropores. The sorption capacity of pyrolytic carbon black was also increased by activation. The uptake of CO2 was three times and for cyclohexane ten times higher in activated carbon black than in the non-activated one. Specific surface areas evaluated from linearized forms of Langmuir isotherm and the BET isotherm revealed that for both methods, the values are comparable for non-activated carbon black measured by CO2 and for activated carbon black measured by cyclohexane. It was found out that the N2 sorption capacity of carbon black depends only on its specific surface area size, contrary to CO2 sorption capacity, which is affected by both the size of specific surface area and the nature of carbon black.